Laser Metal Deposition of Rene 80—Microstructure and Solidification Behavior Modelling
- Location
-
Deutsche Nationalbibliothek Frankfurt am Main
- Extent
-
Online-Ressource
- Language
-
Englisch
- Bibliographic citation
-
In: Micromachines, 15, 10, S. 1-14
- Event
-
Veröffentlichung
- (where)
-
Berlin
- (who)
-
Bundesanstalt für Materialforschung und -prüfung (BAM)
- (when)
-
2024
- Creator
- DOI
-
10.3390/mi15101234
- URN
-
urn:nbn:de:kobv:b43-612095
- Rights
-
Der Zugriff auf das Objekt ist unbeschränkt möglich.
- Last update
-
25.03.2025, 1:51 PM CET
Data provider
This object is provided by:
Deutsche Nationalbibliothek. If you have any questions about the object, please contact the data provider.
Deutsche Nationalbibliothek. If you have any questions about the object, please contact the data provider.
Associated
- Srinivasan, Krishnanand
- Gumenyuk, Andrey
- Rethmeier, Michael
- Bundesanstalt für Materialforschung und -prüfung (BAM)
Time of origin
- 2024
Other Objects (12)
MIG-Schweißen von Magnesiumlegierungen
Influence of the weld pool geometry on solidification cracking in partial penetration high power laser beam welding
Numerical Simulation on the Origin of Solidification Cracking in Laser Welded Thick-Walled Structures
Numerical simulation on the origin of solidification cracking in laser welded thick-walled structures
In situ determination of the critical straining condition for solidification cracking during laser beam welding
Detection of solidification crack formation in laser beam welding videos of sheet metal using neural networks
Untersuchungen zur Ermüdungsfestigkeit von Widerstandspunktschweißverbindungen aus hochfesten Mehrfasenstählen unter Berücksichtigung fertigungsspezifischer Einflüsse : = Fatigue strength investigations for spot welded joints of advanced high strength steels taking account of fabrication-specific influences
Life Cycle Assessment of Fusion Welding Processes—A Case Study of Resistance Spot Welding Versus Laser Beam Welding
Quantitative Evaluation of Ultrasonic Wave Propagation in Inhomogeneous Anisotropic Austenitic Welds using 3D Ray Tracing Method : Numerical and Experimental Validation
Integrale Verfahren der aktiven Infrarotthermografie
Phasenumwandlung und lokale mechanische Eigenschaften von TRIP Stahl beim simulierten und realen Widerstandspunktschweißprozess
Eigenspannungsreduktion in strahlgeschweißten Nähten mittels Spannungsumlagerung durch den Einsatz defokussierter Elektronen- bzw. Laserstrahlen
MIG-Schweißen von Magnesiumlegierungen
Influence of the weld pool geometry on solidification cracking in partial penetration high power laser beam welding
Numerical Simulation on the Origin of Solidification Cracking in Laser Welded Thick-Walled Structures
Numerical simulation on the origin of solidification cracking in laser welded thick-walled structures
In situ determination of the critical straining condition for solidification cracking during laser beam welding
Detection of solidification crack formation in laser beam welding videos of sheet metal using neural networks
Untersuchungen zur Ermüdungsfestigkeit von Widerstandspunktschweißverbindungen aus hochfesten Mehrfasenstählen unter Berücksichtigung fertigungsspezifischer Einflüsse : = Fatigue strength investigations for spot welded joints of advanced high strength steels taking account of fabrication-specific influences
Life Cycle Assessment of Fusion Welding Processes—A Case Study of Resistance Spot Welding Versus Laser Beam Welding
Quantitative Evaluation of Ultrasonic Wave Propagation in Inhomogeneous Anisotropic Austenitic Welds using 3D Ray Tracing Method : Numerical and Experimental Validation
Integrale Verfahren der aktiven Infrarotthermografie
Phasenumwandlung und lokale mechanische Eigenschaften von TRIP Stahl beim simulierten und realen Widerstandspunktschweißprozess
Eigenspannungsreduktion in strahlgeschweißten Nähten mittels Spannungsumlagerung durch den Einsatz defokussierter Elektronen- bzw. Laserstrahlen
MIG-Schweißen von Magnesiumlegierungen
Influence of the weld pool geometry on solidification cracking in partial penetration high power laser beam welding
Numerical Simulation on the Origin of Solidification Cracking in Laser Welded Thick-Walled Structures
Numerical simulation on the origin of solidification cracking in laser welded thick-walled structures
In situ determination of the critical straining condition for solidification cracking during laser beam welding
Detection of solidification crack formation in laser beam welding videos of sheet metal using neural networks
Untersuchungen zur Ermüdungsfestigkeit von Widerstandspunktschweißverbindungen aus hochfesten Mehrfasenstählen unter Berücksichtigung fertigungsspezifischer Einflüsse : = Fatigue strength investigations for spot welded joints of advanced high strength steels taking account of fabrication-specific influences
Life Cycle Assessment of Fusion Welding Processes—A Case Study of Resistance Spot Welding Versus Laser Beam Welding
Quantitative Evaluation of Ultrasonic Wave Propagation in Inhomogeneous Anisotropic Austenitic Welds using 3D Ray Tracing Method : Numerical and Experimental Validation
Integrale Verfahren der aktiven Infrarotthermografie
Phasenumwandlung und lokale mechanische Eigenschaften von TRIP Stahl beim simulierten und realen Widerstandspunktschweißprozess