Influence of the weld pool geometry on solidification cracking in partial penetration high power laser beam welding
- Location
-
Deutsche Nationalbibliothek Frankfurt am Main
- Extent
-
Online-Ressource
- Language
-
Englisch
- Bibliographic citation
-
In: 12TH CIRP Conference on photonic technologies (LANE 2022), 111, S. 397-400
- Event
-
Veröffentlichung
- (where)
-
Berlin
- (who)
-
Bundesanstalt für Materialforschung und -prüfung (BAM)
- (when)
-
2022
- Creator
- DOI
-
10.1016/j.procir.2022.08.174
- URN
-
urn:nbn:de:kobv:b43-563940
- Rights
-
Der Zugriff auf das Objekt ist unbeschränkt möglich.
- Last update
-
25.03.2025, 1:44 PM CET
Data provider
This object is provided by:
Deutsche Nationalbibliothek. If you have any questions about the object, please contact the data provider.
Deutsche Nationalbibliothek. If you have any questions about the object, please contact the data provider.
Associated
- Bakir, Nasim
- Üstündag, Ömer
- Gumenyuk, Andrey
- Rethmeier, Michael
- Bundesanstalt für Materialforschung und -prüfung (BAM)
Time of origin
- 2022
Other Objects (12)
Numerical Simulation on the Origin of Solidification Cracking in Laser Welded Thick-Walled Structures
Numerical simulation on the origin of solidification cracking in laser welded thick-walled structures
In situ determination of the critical straining condition for solidification cracking during laser beam welding
Grain refinement in aluminium GTA welds
Evaluation of narrowed weld pool shapes and their effect on resulting potential defects during deep penetration laser beam welding
Full penetration hybrid laser arc welding of up to 28 mm thick S355 plates using electromagnetic weld pool support
Full penetration hybrid laser arc welding of up to 28 mm thick S355 plates using electromagnetic weld pool support
Evaluation of narrowed weld pool shapes and their effect on resulting potential defects during deep penetration laser beam welding
Numerical analysis of hot cracking in laser-hybrid welded tubes
Full penetration laser beam welding of thick duplex steel plates with electromagnetic weld pool support
Laser Metal Deposition of Rene 80—Microstructure and Solidification Behavior Modelling
Quantitative Evaluation of Ultrasonic Wave Propagation in Inhomogeneous Anisotropic Austenitic Welds using 3D Ray Tracing Method : Numerical and Experimental Validation
Numerical Simulation on the Origin of Solidification Cracking in Laser Welded Thick-Walled Structures
Numerical simulation on the origin of solidification cracking in laser welded thick-walled structures
In situ determination of the critical straining condition for solidification cracking during laser beam welding
Grain refinement in aluminium GTA welds
Evaluation of narrowed weld pool shapes and their effect on resulting potential defects during deep penetration laser beam welding
Full penetration hybrid laser arc welding of up to 28 mm thick S355 plates using electromagnetic weld pool support
Full penetration hybrid laser arc welding of up to 28 mm thick S355 plates using electromagnetic weld pool support
Evaluation of narrowed weld pool shapes and their effect on resulting potential defects during deep penetration laser beam welding
Numerical analysis of hot cracking in laser-hybrid welded tubes
Full penetration laser beam welding of thick duplex steel plates with electromagnetic weld pool support
Laser Metal Deposition of Rene 80—Microstructure and Solidification Behavior Modelling
Quantitative Evaluation of Ultrasonic Wave Propagation in Inhomogeneous Anisotropic Austenitic Welds using 3D Ray Tracing Method : Numerical and Experimental Validation
Numerical Simulation on the Origin of Solidification Cracking in Laser Welded Thick-Walled Structures
Numerical simulation on the origin of solidification cracking in laser welded thick-walled structures
In situ determination of the critical straining condition for solidification cracking during laser beam welding
Grain refinement in aluminium GTA welds
Evaluation of narrowed weld pool shapes and their effect on resulting potential defects during deep penetration laser beam welding
Full penetration hybrid laser arc welding of up to 28 mm thick S355 plates using electromagnetic weld pool support
Full penetration hybrid laser arc welding of up to 28 mm thick S355 plates using electromagnetic weld pool support
Evaluation of narrowed weld pool shapes and their effect on resulting potential defects during deep penetration laser beam welding
Numerical analysis of hot cracking in laser-hybrid welded tubes
Full penetration laser beam welding of thick duplex steel plates with electromagnetic weld pool support
Laser Metal Deposition of Rene 80—Microstructure and Solidification Behavior Modelling