New inorganic inhibitors derived from cefotaxime to enhance corrosion resistance of mild steel in 3% NaCl
- Location
-
Deutsche Nationalbibliothek Frankfurt am Main
- Extent
-
1 Online-Ressource.
- Language
-
Englisch
- Bibliographic citation
-
New inorganic inhibitors derived from cefotaxime to enhance corrosion resistance of mild steel in 3% NaCl ; volume:14 ; number:1 ; day:10 ; month:1 ; year:2024 ; pages:1-20 ; date:12.2024
Scientific reports ; 14, Heft 1 (10.1.2024), 1-20, 12.2024
- Creator
-
Abd El-Zahir, Mustafa S.
Soliman, Mohamed H. A.
ELKady, Hamdy A.
El-Sakka, Sahar S. A.
Orabi, Adel S.
- Contributor
-
SpringerLink (Online service)
- DOI
-
10.1038/s41598-024-51275-5
- URN
-
urn:nbn:de:101:1-2024032509465398288197
- Rights
-
Open Access; Der Zugriff auf das Objekt ist unbeschränkt möglich.
- Last update
-
14.08.2025, 10:57 AM CEST
Data provider
This object is provided by:
Deutsche Nationalbibliothek. If you have any questions about the object, please contact the data provider.
Deutsche Nationalbibliothek. If you have any questions about the object, please contact the data provider.
Associated
- Abd El-Zahir, Mustafa S.
- Soliman, Mohamed H. A.
- ELKady, Hamdy A.
- El-Sakka, Sahar S. A.
- Orabi, Adel S.
- SpringerLink (Online service)
Other Objects (12)
Corrosion resistance of steels against inorganic acids
Erosion-Corrosion Mechanisms of Engineering Steels in Different NaCl Concentrations
The influence of NaCl and CaCl 2 induced high temperature corrosion on the aqueous corrosion resistance of stainless steels
A comparative study on corrosion kinetic parameter estimation methods for the early stage corrosion of Q345B steel in 3.5wt% NaCl solution
Influence of polyolefin modified by Y2O3 as protective coatings against carbon steel corrosion into 3.5% NaCl media
Corrosion of reinforcing steel
Corrosion of prestressing steel
Comparison of Cycling High Temperature Corrosion at 650°C in the Presence of NaCl of Various Austenitic Stainless Steels
Mechanism of Carbon Steel Corrosion in Accelerated Corrosion Tests
Hybrid inorganic–organic coatings enhancing glass corrosion resistance
Metal Dusting Corrosion of Carbon Steel
In situ monitoring of stress corrosion at the Alloy 625/NaCl interface
Corrosion resistance of steels against inorganic acids
Erosion-Corrosion Mechanisms of Engineering Steels in Different NaCl Concentrations
The influence of NaCl and CaCl 2 induced high temperature corrosion on the aqueous corrosion resistance of stainless steels
A comparative study on corrosion kinetic parameter estimation methods for the early stage corrosion of Q345B steel in 3.5wt% NaCl solution
Influence of polyolefin modified by Y2O3 as protective coatings against carbon steel corrosion into 3.5% NaCl media
Corrosion of reinforcing steel
Corrosion of prestressing steel
Comparison of Cycling High Temperature Corrosion at 650°C in the Presence of NaCl of Various Austenitic Stainless Steels
Mechanism of Carbon Steel Corrosion in Accelerated Corrosion Tests
Hybrid inorganic–organic coatings enhancing glass corrosion resistance
Metal Dusting Corrosion of Carbon Steel
In situ monitoring of stress corrosion at the Alloy 625/NaCl interface
Corrosion resistance of steels against inorganic acids
Erosion-Corrosion Mechanisms of Engineering Steels in Different NaCl Concentrations
The influence of NaCl and CaCl 2 induced high temperature corrosion on the aqueous corrosion resistance of stainless steels
A comparative study on corrosion kinetic parameter estimation methods for the early stage corrosion of Q345B steel in 3.5wt% NaCl solution
Influence of polyolefin modified by Y2O3 as protective coatings against carbon steel corrosion into 3.5% NaCl media
Corrosion of reinforcing steel
Corrosion of prestressing steel
Comparison of Cycling High Temperature Corrosion at 650°C in the Presence of NaCl of Various Austenitic Stainless Steels
Mechanism of Carbon Steel Corrosion in Accelerated Corrosion Tests
Hybrid inorganic–organic coatings enhancing glass corrosion resistance
Metal Dusting Corrosion of Carbon Steel