Stress Corrosion Cracking of Manganese Bronze in Water ; volume:24 ; number:6 ; day:1 ; month:10 ; year:2024 ; pages:2555-2560 ; date:12.2024
Journal of failure analysis and prevention ; 24, Heft 6 (1.10.2024), 2555-2560, 12.2024
- Creator
-
Manz, Olaf
Kral, Milo
- Contributor
-
SpringerLink (Online service)
- DOI
-
10.1007/s11668-024-02041-2
- URN
-
urn:nbn:de:101:1-2503010634298.672927224504
- Rights
-
Open Access; Der Zugriff auf das Objekt ist unbeschränkt möglich.
- Last update
-
15.08.2025, 7:27 AM CEST
Data provider
This object is provided by:
Deutsche Nationalbibliothek. If you have any questions about the object, please contact the data provider.
Deutsche Nationalbibliothek. If you have any questions about the object, please contact the data provider.
Associated
- Manz, Olaf
- Kral, Milo
- SpringerLink (Online service)
Other Objects (12)
Effect of chloride ion concentration on stress corrosion cracking and electrochemical corrosion of high manganese steel
Corrosion, stress corrosion cracking and corrosion fatigue behavior of magnesium alloy bioimplants
Nanoscale mechanisms of stress-corrosion cracking of 7xxx Al-alloys
XGBoost model for the quantitative assessment of stress corrosion cracking
Stress corrosion cracking and corrosion fatigue of steam-turbine rotor and blade materials : COST
Chlorine-Induced Stress Corrosion Cracking of Single Crystal Superalloys at 550 °C
Probing intergranular mixed transgranular stress corrosion cracking under the high constant load
Corrosion evaluation of welded nickel aluminum bronze and manganese aluminum bronze in synthetic sea water
General corrosion and stress corrosion cracking studies on carbon steels for application in nuclear waste disposal containers
Localized corrosion and stress corrosion cracking of stainless steels in halides other than chlorides solutions: a review
Hydrogen‐induced stress corrosion cracking studied by the novel tuning‐fork test method
Study on corrosion, hydrogen permeation, and stress corrosion cracking behaviours of AISI 4135 steel in the tidal zone
Effect of chloride ion concentration on stress corrosion cracking and electrochemical corrosion of high manganese steel
Corrosion, stress corrosion cracking and corrosion fatigue behavior of magnesium alloy bioimplants
Nanoscale mechanisms of stress-corrosion cracking of 7xxx Al-alloys
XGBoost model for the quantitative assessment of stress corrosion cracking
Stress corrosion cracking and corrosion fatigue of steam-turbine rotor and blade materials : COST
Chlorine-Induced Stress Corrosion Cracking of Single Crystal Superalloys at 550 °C
Probing intergranular mixed transgranular stress corrosion cracking under the high constant load
Corrosion evaluation of welded nickel aluminum bronze and manganese aluminum bronze in synthetic sea water
General corrosion and stress corrosion cracking studies on carbon steels for application in nuclear waste disposal containers
Localized corrosion and stress corrosion cracking of stainless steels in halides other than chlorides solutions: a review
Hydrogen‐induced stress corrosion cracking studied by the novel tuning‐fork test method
Study on corrosion, hydrogen permeation, and stress corrosion cracking behaviours of AISI 4135 steel in the tidal zone
Effect of chloride ion concentration on stress corrosion cracking and electrochemical corrosion of high manganese steel
Corrosion, stress corrosion cracking and corrosion fatigue behavior of magnesium alloy bioimplants
Nanoscale mechanisms of stress-corrosion cracking of 7xxx Al-alloys
XGBoost model for the quantitative assessment of stress corrosion cracking
Stress corrosion cracking and corrosion fatigue of steam-turbine rotor and blade materials : COST
Chlorine-Induced Stress Corrosion Cracking of Single Crystal Superalloys at 550 °C
Probing intergranular mixed transgranular stress corrosion cracking under the high constant load
Corrosion evaluation of welded nickel aluminum bronze and manganese aluminum bronze in synthetic sea water
General corrosion and stress corrosion cracking studies on carbon steels for application in nuclear waste disposal containers
Localized corrosion and stress corrosion cracking of stainless steels in halides other than chlorides solutions: a review
Hydrogen‐induced stress corrosion cracking studied by the novel tuning‐fork test method