Numerical and experimental assessment of liquid metal embrittlement in externally loaded spot welds
- Standort
-
Deutsche Nationalbibliothek Frankfurt am Main
- Umfang
-
1 Online-Ressource.
- Sprache
-
Englisch
- Erschienen in
-
Numerical and experimental assessment of liquid metal embrittlement in externally loaded spot welds ; volume:68 ; number:10 ; day:30 ; month:1 ; year:2024 ; pages:2713-2722 ; date:10.2024
Welding in the world ; 68, Heft 10 (30.1.2024), 2713-2722, 10.2024
- Urheber
-
Prabitz, Konstantin Manuel
Antretter, Thomas
Rethmeier, Michael
El-Sari, Bassel
Schubert, Holger
Hilpert, Benjamin
Gruber, Martin
Sierlinger, Robert
Ecker, Werner
- Beteiligte Personen und Organisationen
-
SpringerLink (Online service)
- DOI
-
10.1007/s40194-024-01696-7
- URN
-
urn:nbn:de:101:1-2411272116478.556689579869
- Rechteinformation
-
Open Access; Der Zugriff auf das Objekt ist unbeschränkt möglich.
- Letzte Aktualisierung
-
15.08.2025, 07:28 MESZ
Datenpartner
Dieses Objekt wird bereitgestellt von:
Deutsche Nationalbibliothek. Bei Fragen zum Objekt wenden Sie sich bitte an den Datenpartner.
Deutsche Nationalbibliothek. Bei Fragen zum Objekt wenden Sie sich bitte an den Datenpartner.
Beteiligte
- Prabitz, Konstantin Manuel
- Antretter, Thomas
- Rethmeier, Michael
- El-Sari, Bassel
- Schubert, Holger
- Hilpert, Benjamin
- Gruber, Martin
- Sierlinger, Robert
- Ecker, Werner
- SpringerLink (Online service)
Ähnliche Objekte (12)
Numerical and experimental assessment of liquid metal embrittlement in externally loaded spot welds
Numerical and experimental assessment of liquid metal embrittlement in externally loaded spot welds
Laser weld spot detection based on YOLO-weld
Influence of liquid metal embrittlement on the failure behavior of dissimilar spot welds with advanced high-strength steel: A component study
Influence of liquid metal embrittlement on the failure behavior of dissimilar spot welds with advanced high-strength steel: A component study
Failure Characterization of Laser Welds and Spot Welds under Combined Loading Conditions
Liquid metal embrittlement of advanced high strength steels during resistance spot welding
Effect of Weld Schedule on the Residual Stress Distribution of Boron Steel Spot Welds
Reliable detection of stick welds at resistance spot welding
Automated Spot Weld Testing using a Smart Robotic System
Estimation of the Incidence of Liquid Metal Embrittlement Crack in 3rd Generation Advanced High Strength Steel During Resistance Spot Welding using 2D and 3D Weld Lobe Curve
Neutron irradiation embrittlement of reactor pressure vessel steel 20 MnMoNi55 [MnMoNi] weld
Numerical and experimental assessment of liquid metal embrittlement in externally loaded spot welds
Numerical and experimental assessment of liquid metal embrittlement in externally loaded spot welds
Laser weld spot detection based on YOLO-weld
Influence of liquid metal embrittlement on the failure behavior of dissimilar spot welds with advanced high-strength steel: A component study
Influence of liquid metal embrittlement on the failure behavior of dissimilar spot welds with advanced high-strength steel: A component study
Failure Characterization of Laser Welds and Spot Welds under Combined Loading Conditions
Liquid metal embrittlement of advanced high strength steels during resistance spot welding
Effect of Weld Schedule on the Residual Stress Distribution of Boron Steel Spot Welds
Reliable detection of stick welds at resistance spot welding
Automated Spot Weld Testing using a Smart Robotic System
Estimation of the Incidence of Liquid Metal Embrittlement Crack in 3rd Generation Advanced High Strength Steel During Resistance Spot Welding using 2D and 3D Weld Lobe Curve
Neutron irradiation embrittlement of reactor pressure vessel steel 20 MnMoNi55 [MnMoNi] weld
Numerical and experimental assessment of liquid metal embrittlement in externally loaded spot welds
Numerical and experimental assessment of liquid metal embrittlement in externally loaded spot welds
Laser weld spot detection based on YOLO-weld
Influence of liquid metal embrittlement on the failure behavior of dissimilar spot welds with advanced high-strength steel: A component study
Influence of liquid metal embrittlement on the failure behavior of dissimilar spot welds with advanced high-strength steel: A component study
Failure Characterization of Laser Welds and Spot Welds under Combined Loading Conditions
Liquid metal embrittlement of advanced high strength steels during resistance spot welding
Effect of Weld Schedule on the Residual Stress Distribution of Boron Steel Spot Welds
Reliable detection of stick welds at resistance spot welding
Automated Spot Weld Testing using a Smart Robotic System
Estimation of the Incidence of Liquid Metal Embrittlement Crack in 3rd Generation Advanced High Strength Steel During Resistance Spot Welding using 2D and 3D Weld Lobe Curve