Local relaxation of residual stress in high-strength steel welded joints treated by HFMI
- Location
-
Deutsche Nationalbibliothek Frankfurt am Main
- Extent
-
1 Online-Ressource.
- Language
-
Englisch
- Bibliographic citation
-
Local relaxation of residual stress in high-strength steel welded joints treated by HFMI ; volume:68 ; number:8 ; day:3 ; month:6 ; year:2024 ; pages:2187-2202 ; date:8.2024
Welding in the world ; 68, Heft 8 (3.6.2024), 2187-2202, 8.2024
- Creator
-
Ono, Yuki
Remes, Heikki
Kinoshita, Koji
Yıldırım, Halid Can
Nussbaumer, Alain
- Contributor
-
SpringerLink (Online service)
- DOI
-
10.1007/s40194-024-01789-3
- URN
-
urn:nbn:de:101:1-2409252110471.509245937820
- Rights
-
Open Access; Der Zugriff auf das Objekt ist unbeschränkt möglich.
- Last update
-
15.08.2025, 7:35 AM CEST
Data provider
This object is provided by:
Deutsche Nationalbibliothek. If you have any questions about the object, please contact the data provider.
Deutsche Nationalbibliothek. If you have any questions about the object, please contact the data provider.
Associated
- Ono, Yuki
- Remes, Heikki
- Kinoshita, Koji
- Yıldırım, Halid Can
- Nussbaumer, Alain
- SpringerLink (Online service)
Other Objects (12)
Welded connections at high-strength steel hollow section joints
Welded connections at high‐strength steel hollow section joints
Numerical analyses on welded joints at high‐strength steels
Influence of Heat Control on Properties and Residual Stresses of Additive-Welded High-Strength Steel Components
Numerical Analysis of Welding Residual Stress Relaxation in High-Strength Multilayer Weldment Under Fatigue Loads
Hydrogen-assisted cracking of GMA welded 960 MPa grade high-strength steels
High-strength steel S960QC welded with rare earth nanoparticle coated filler wire
Experimental investigations of residual stresses in thick high‐strength steel plates
Matching effect on fatigue crack growth behaviour of high-strength steels GMA welded joints
A new design model for welded joints : Experimental investigations of welds on high‐strength steels
Effect of processing temperatures on the properties of a high-strength steel welded by FSW
Determination of residual stress evolution during repair welding of high-strength steel components
Welded connections at high-strength steel hollow section joints
Welded connections at high‐strength steel hollow section joints
Numerical analyses on welded joints at high‐strength steels
Influence of Heat Control on Properties and Residual Stresses of Additive-Welded High-Strength Steel Components
Numerical Analysis of Welding Residual Stress Relaxation in High-Strength Multilayer Weldment Under Fatigue Loads
Hydrogen-assisted cracking of GMA welded 960 MPa grade high-strength steels
High-strength steel S960QC welded with rare earth nanoparticle coated filler wire
Experimental investigations of residual stresses in thick high‐strength steel plates
Matching effect on fatigue crack growth behaviour of high-strength steels GMA welded joints
A new design model for welded joints : Experimental investigations of welds on high‐strength steels
Effect of processing temperatures on the properties of a high-strength steel welded by FSW
Determination of residual stress evolution during repair welding of high-strength steel components
Welded connections at high-strength steel hollow section joints
Welded connections at high‐strength steel hollow section joints
Numerical analyses on welded joints at high‐strength steels
Influence of Heat Control on Properties and Residual Stresses of Additive-Welded High-Strength Steel Components
Numerical Analysis of Welding Residual Stress Relaxation in High-Strength Multilayer Weldment Under Fatigue Loads
Hydrogen-assisted cracking of GMA welded 960 MPa grade high-strength steels
High-strength steel S960QC welded with rare earth nanoparticle coated filler wire
Experimental investigations of residual stresses in thick high‐strength steel plates
Matching effect on fatigue crack growth behaviour of high-strength steels GMA welded joints
A new design model for welded joints : Experimental investigations of welds on high‐strength steels
Effect of processing temperatures on the properties of a high-strength steel welded by FSW