Drying of Lithium‐Ion Battery Anodes for Use in High‐Energy Cells: Influence of Electrode Thickness on Drying Time, Adhesion, and Crack Formation
When fabricating battery electrodes, their properties are strongly determined by the adjusted drying parameters. This does not only affect their microstructure in terms of adhesion, but also influences cell performance. The reason is found to be the binder transported to the surface during drying. Herein, it is shown that when thicker electrodes are processed, new challenges arise. On the one hand, loss of adhesion associated with certain drying conditions becomes a more serious problem; on the other hand, cracking occurs at a certain drying rate and with increasing electrode thickness.
- Standort
-
Deutsche Nationalbibliothek Frankfurt am Main
- Umfang
-
Online-Ressource
- Sprache
-
Englisch
- Erschienen in
-
Drying of Lithium‐Ion Battery Anodes for Use in High‐Energy Cells: Influence of Electrode Thickness on Drying Time, Adhesion, and Crack Formation ; volume:7 ; number:11 ; year:2019 ; extent:11
Energy technology ; 7, Heft 11 (2019) (gesamt 11)
- Urheber
-
Kumberg, Jana
Müller, Marcus
Diehm, Ralf
Spiegel, Sandro
Wachsmann, Christian
Bauer, Werner
Scharfer, Philip
Schabel, Wilhelm
- DOI
-
10.1002/ente.201900722
- URN
-
urn:nbn:de:101:1-2022072808240136546920
- Rechteinformation
-
Open Access; Der Zugriff auf das Objekt ist unbeschränkt möglich.
- Letzte Aktualisierung
-
15.08.2025, 07:36 MESZ
Datenpartner
Dieses Objekt wird bereitgestellt von:
Deutsche Nationalbibliothek. Bei Fragen zum Objekt wenden Sie sich bitte an den Datenpartner.
Deutsche Nationalbibliothek. Bei Fragen zum Objekt wenden Sie sich bitte an den Datenpartner.
Beteiligte
- Kumberg, Jana
- Müller, Marcus
- Diehm, Ralf
- Spiegel, Sandro
- Wachsmann, Christian
- Bauer, Werner
- Scharfer, Philip
- Schabel, Wilhelm
Ähnliche Objekte (12)
Morphological instabilities in drying colloids
Reduced Drying Time of Anodes for Lithium‐Ion Batteries through Simultaneous Multilayer Coating
Ergebnisse nach arthroskopischer Resektion einer Plica synovialis mediopatellaris
Meniskusnaht des Kniegelenks mit einem langsam resorbierbaren Nahtmaterial (Panacryl) : makroskopische, histologische und rasterelektronenmikroskopische Untersuchungen am Schaf
Berechnung dreidimensionaler Strömungsfelder der transthorakalen Defibrillation im menschlichen Körper mit der Finite-Elemente-Methode
Zur Ikonisierung komplexer Sprachzeichen in der Medienwelt - das Beispiel Infografik
Juliane Schröter. 2021. Linguistische Argumentationsanalyse. (KEGLI 26). Heidelberg: Winter Verlag. 100 S.
Process and Drying Behavior Toward Higher Drying Rates of Hard Carbon Anodes for Sodium‐Ion Batteries with Different Particle Sizes: An Experimental Study in Comparison to Graphite for Lithium‐Ion‐Batteries
Additive Influence on Binder Migration in Electrode Drying
Botschaft der Hoffnung oder Worum geht es überhaupt in der Bibel?
Diskurszukünfte. 10. Jahrestagung des Forschungsnetzwerks "Sprache und Wissen". Jubiläums- und Programmzeitschrift
From 0 to 6 GHz in 30 minutes: Bootstrapping your SDR experience: Start from scratch today, hack the EM spectrum tomorrow!
Morphological instabilities in drying colloids
Reduced Drying Time of Anodes for Lithium‐Ion Batteries through Simultaneous Multilayer Coating
Ergebnisse nach arthroskopischer Resektion einer Plica synovialis mediopatellaris
Meniskusnaht des Kniegelenks mit einem langsam resorbierbaren Nahtmaterial (Panacryl) : makroskopische, histologische und rasterelektronenmikroskopische Untersuchungen am Schaf
Berechnung dreidimensionaler Strömungsfelder der transthorakalen Defibrillation im menschlichen Körper mit der Finite-Elemente-Methode
Zur Ikonisierung komplexer Sprachzeichen in der Medienwelt - das Beispiel Infografik
Juliane Schröter. 2021. Linguistische Argumentationsanalyse. (KEGLI 26). Heidelberg: Winter Verlag. 100 S.
Process and Drying Behavior Toward Higher Drying Rates of Hard Carbon Anodes for Sodium‐Ion Batteries with Different Particle Sizes: An Experimental Study in Comparison to Graphite for Lithium‐Ion‐Batteries
Additive Influence on Binder Migration in Electrode Drying
Botschaft der Hoffnung oder Worum geht es überhaupt in der Bibel?
Diskurszukünfte. 10. Jahrestagung des Forschungsnetzwerks "Sprache und Wissen". Jubiläums- und Programmzeitschrift
From 0 to 6 GHz in 30 minutes: Bootstrapping your SDR experience: Start from scratch today, hack the EM spectrum tomorrow!
Morphological instabilities in drying colloids
Reduced Drying Time of Anodes for Lithium‐Ion Batteries through Simultaneous Multilayer Coating
Ergebnisse nach arthroskopischer Resektion einer Plica synovialis mediopatellaris
Meniskusnaht des Kniegelenks mit einem langsam resorbierbaren Nahtmaterial (Panacryl) : makroskopische, histologische und rasterelektronenmikroskopische Untersuchungen am Schaf
Berechnung dreidimensionaler Strömungsfelder der transthorakalen Defibrillation im menschlichen Körper mit der Finite-Elemente-Methode
Zur Ikonisierung komplexer Sprachzeichen in der Medienwelt - das Beispiel Infografik
Juliane Schröter. 2021. Linguistische Argumentationsanalyse. (KEGLI 26). Heidelberg: Winter Verlag. 100 S.
Process and Drying Behavior Toward Higher Drying Rates of Hard Carbon Anodes for Sodium‐Ion Batteries with Different Particle Sizes: An Experimental Study in Comparison to Graphite for Lithium‐Ion‐Batteries
Additive Influence on Binder Migration in Electrode Drying
Botschaft der Hoffnung oder Worum geht es überhaupt in der Bibel?
Diskurszukünfte. 10. Jahrestagung des Forschungsnetzwerks "Sprache und Wissen". Jubiläums- und Programmzeitschrift