Combination of synchrotron computed tomography and acoustic emission measurements for cyclic loading of fibre-reinforced composites
- Location
-
Deutsche Nationalbibliothek Frankfurt am Main
- Extent
-
Online-Ressource
- Language
-
Englisch
- Notes
-
In: EWGAE 2018 - 33rd European Conference on Acoustic Emission, Senlis, France, 12-14 September 2018, S.
- Event
-
Veröffentlichung
- (where)
-
Augsburg, Senlis
- (who)
-
Universität Augsburg, Cetim
- (when)
-
2018
- Creator
-
Potstada, Philipp
Rosini, Sebastian
Mavrogordato, Mark
Sinclair, Ian
Spearing, S. Mark
Sause, Markus
- URN
-
urn:nbn:de:bvb:384-opus4-771430
- Rights
-
Der Zugriff auf das Objekt ist unbeschränkt möglich.
- Last update
-
25.03.2025, 1:46 PM CET
Data provider
This object is provided by:
Deutsche Nationalbibliothek. If you have any questions about the object, please contact the data provider.
Deutsche Nationalbibliothek. If you have any questions about the object, please contact the data provider.
Associated
- Potstada, Philipp
- Rosini, Sebastian
- Mavrogordato, Mark
- Sinclair, Ian
- Spearing, S. Mark
- Sause, Markus
- Universität Augsburg, Cetim
Time of origin
- 2018
Other Objects (12)
On use of signal features for acoustic emission source identification in fibre-reinforced composites
Identification of failure mechanisms in hybrid materials utilizing pattern recognition techniques applied to acoustic emission signals
Cross-validation of single filament failure by acoustic emission and high-resolution synchrotron computed tomography
Detection of crack initiation for fracture toughness evaluation of thermoset and thermoplastic fibre-reinforced materials
Combined acoustic emission and thermographic testing of fibre composites
Comparison of carbon composite failure with thermoset and thermoplastic matrix by in-situ monitoring using computed tomography and acoustic emission
Acoustic emission source identification in large scale fibre reinforced composites
Scan quality optimization for measuring Fiber-Metal-Laminates with X-Ray computed tomography
Determination of crack surface orientation in carbon fibre reinforced polymers by measuring electromagnetic emission
In-situ Überwachung von Faserverbundwerkstoffen
Identification of damage onset in CFRP laminates under tension-tension fatigue using acoustic emission analysis [Abstract]
Experimentelle und modellhafte Betrachtung des Konsolidierungsprozesses von carbonfaserverstärktem Polyamid-6
On use of signal features for acoustic emission source identification in fibre-reinforced composites
Identification of failure mechanisms in hybrid materials utilizing pattern recognition techniques applied to acoustic emission signals
Cross-validation of single filament failure by acoustic emission and high-resolution synchrotron computed tomography
Detection of crack initiation for fracture toughness evaluation of thermoset and thermoplastic fibre-reinforced materials
Combined acoustic emission and thermographic testing of fibre composites
Comparison of carbon composite failure with thermoset and thermoplastic matrix by in-situ monitoring using computed tomography and acoustic emission
Acoustic emission source identification in large scale fibre reinforced composites
Scan quality optimization for measuring Fiber-Metal-Laminates with X-Ray computed tomography
Determination of crack surface orientation in carbon fibre reinforced polymers by measuring electromagnetic emission
In-situ Überwachung von Faserverbundwerkstoffen
Identification of damage onset in CFRP laminates under tension-tension fatigue using acoustic emission analysis [Abstract]
Experimentelle und modellhafte Betrachtung des Konsolidierungsprozesses von carbonfaserverstärktem Polyamid-6
On use of signal features for acoustic emission source identification in fibre-reinforced composites
Identification of failure mechanisms in hybrid materials utilizing pattern recognition techniques applied to acoustic emission signals
Cross-validation of single filament failure by acoustic emission and high-resolution synchrotron computed tomography
Detection of crack initiation for fracture toughness evaluation of thermoset and thermoplastic fibre-reinforced materials
Combined acoustic emission and thermographic testing of fibre composites
Comparison of carbon composite failure with thermoset and thermoplastic matrix by in-situ monitoring using computed tomography and acoustic emission
Acoustic emission source identification in large scale fibre reinforced composites
Scan quality optimization for measuring Fiber-Metal-Laminates with X-Ray computed tomography
Determination of crack surface orientation in carbon fibre reinforced polymers by measuring electromagnetic emission
In-situ Überwachung von Faserverbundwerkstoffen
Identification of damage onset in CFRP laminates under tension-tension fatigue using acoustic emission analysis [Abstract]