Ultrasonic detection of spall damage induced by low-velocity repeated impact
Abstract: This paper address the examination of spall damage in medium carbon steel subjected to a repeated impact testing. The experiments were performed well below the threshold spall-stress of 2.6 GPa and the damage introduced in the subsurface volume was investigated using the low frequency scanning acoustic microscopy. Based on B- and C-scan images (the images taken along and perpendicular to the impact surface) we made a qualitative and semi-quantitative evaluation of the damage type (voids in a ductile material or cracks in a brittle one) and its distribution. We found the spall damage development dependent on the amplitude and the duration of the stress pulses. In particular, we proved that the high, long stress pulses induce damage that resembles tensile failure of material, in which voids or cracks nucleate along the spall plane to form macro-cracks. This explains why spall-damage is not seen when the first impact is below the characteristic threshold spall-stress. However, when the tests consist of more than four impacts the spall damage is produced already under stress below the threshold-value.
- Location
-
Deutsche Nationalbibliothek Frankfurt am Main
- Extent
-
Online-Ressource
- Language
-
Englisch
- Bibliographic citation
-
Ultrasonic detection of spall damage induced by low-velocity repeated impact ; volume:2 ; number:4 ; year:2012 ; pages:650-655 ; extent:6
Open engineering ; 2, Heft 4 (2012), 650-655 (gesamt 6)
- Creator
-
Nishimura, Naoya
Murase, Katsuhiko
Ito, Toshihiro
Watanabe, Takeru
Nowak, Roman
- DOI
-
10.2478/s13531-012-0013-5
- URN
-
urn:nbn:de:101:1-2412141715354.962868155101
- Rights
-
Open Access; Der Zugriff auf das Objekt ist unbeschränkt möglich.
- Last update
-
01.01.0017, 6:34 AM CET
Data provider
Deutsche Nationalbibliothek. If you have any questions about the object, please contact the data provider.
Associated
- Nishimura, Naoya
- Murase, Katsuhiko
- Ito, Toshihiro
- Watanabe, Takeru
- Nowak, Roman
Other Objects (12)
Simplified Ultrasonic Damage Detection in Fluid-Filled Pipes
Correlating Ultrasonic Velocity in DC04 with Microstructure for Quantification of Ductile Damage
Low-Velocity Impact Damage Quantification on Sandwich Panels by Thermographic and Ultrasonic Procedures
Damage detection in multi-layered plates using ultrasonic guided waves
Damage evolution in GLARE fibre-metal laminate under repeated low-velocity impact tests
Repeated tracheal tube damage due to an ultrasonic bone aspirator in Le Fort I osteotomy
The repeated low-velocity impact response and damage accumulation of shape memory alloy hybrid composite laminates
Damage accumulation and failure mechanism of glass/epoxy composite laminates subjected to repeated low velocity impacts
Impact Damage Detection in Laminate and Honeycomb CFRPs using Lamb Wave Ultrasonic Sensing
Towards interpretable machine learning for automated damage detection based on ultrasonic guided waves
Radiation damage of polymers in ultrasonic fields
Damage Detection in Multiple RC Structures Based on Embedded Ultrasonic Sensors and Wavelet Transform
Simplified Ultrasonic Damage Detection in Fluid-Filled Pipes
Correlating Ultrasonic Velocity in DC04 with Microstructure for Quantification of Ductile Damage
Low-Velocity Impact Damage Quantification on Sandwich Panels by Thermographic and Ultrasonic Procedures
Damage detection in multi-layered plates using ultrasonic guided waves
Damage evolution in GLARE fibre-metal laminate under repeated low-velocity impact tests
Repeated tracheal tube damage due to an ultrasonic bone aspirator in Le Fort I osteotomy
The repeated low-velocity impact response and damage accumulation of shape memory alloy hybrid composite laminates
Damage accumulation and failure mechanism of glass/epoxy composite laminates subjected to repeated low velocity impacts
Impact Damage Detection in Laminate and Honeycomb CFRPs using Lamb Wave Ultrasonic Sensing
Towards interpretable machine learning for automated damage detection based on ultrasonic guided waves
Radiation damage of polymers in ultrasonic fields
Damage Detection in Multiple RC Structures Based on Embedded Ultrasonic Sensors and Wavelet Transform
Simplified Ultrasonic Damage Detection in Fluid-Filled Pipes
Correlating Ultrasonic Velocity in DC04 with Microstructure for Quantification of Ductile Damage
Low-Velocity Impact Damage Quantification on Sandwich Panels by Thermographic and Ultrasonic Procedures
Damage detection in multi-layered plates using ultrasonic guided waves
Damage evolution in GLARE fibre-metal laminate under repeated low-velocity impact tests
Repeated tracheal tube damage due to an ultrasonic bone aspirator in Le Fort I osteotomy
The repeated low-velocity impact response and damage accumulation of shape memory alloy hybrid composite laminates
Damage accumulation and failure mechanism of glass/epoxy composite laminates subjected to repeated low velocity impacts
Impact Damage Detection in Laminate and Honeycomb CFRPs using Lamb Wave Ultrasonic Sensing
Towards interpretable machine learning for automated damage detection based on ultrasonic guided waves
Radiation damage of polymers in ultrasonic fields