Chloride‐induced steel corrosion in alkali‐activated fly ash mortar: Increased propensity for corrosion initiation at defects
- Standort
-
Deutsche Nationalbibliothek Frankfurt am Main
- Umfang
-
Online-Ressource
- Sprache
-
Englisch
- Erschienen in
-
Chloride‐induced steel corrosion in alkali‐activated fly ash mortar: Increased propensity for corrosion initiation at defects ; volume:71 ; number:5 ; year:2020 ; pages:749-758 ; extent:10
Materials and corrosion ; 71, Heft 5 (2020), 749-758 (gesamt 10)
- Urheber
- DOI
-
10.1002/maco.202011541
- URN
-
urn:nbn:de:101:1-2022070407051336289919
- Rechteinformation
-
Open Access; Der Zugriff auf das Objekt ist unbeschränkt möglich.
- Letzte Aktualisierung
-
15.08.2025, 07:35 MESZ
Datenpartner
Dieses Objekt wird bereitgestellt von:
Deutsche Nationalbibliothek. Bei Fragen zum Objekt wenden Sie sich bitte an den Datenpartner.
Deutsche Nationalbibliothek. Bei Fragen zum Objekt wenden Sie sich bitte an den Datenpartner.
Beteiligte
- Gluth, Gregor J. G.
- Ebell, Gino
- Hlaváček, Petr
- Mietz, Jürgen
Ähnliche Objekte (12)
Chloride‐induced steel corrosion in alkali‐activated fly ash mortar: Increased propensity for corrosion initiation at defects
Steel corrosion in reinforced alkali‐activated materials
Leaching, carbonation and chloride ingress in reinforced alkali-activated fly ash mortars
Predicting and understanding corrosion in molten chloride salts
Application of electrochemical methods for studying steel corrosion in alkali-activated materials
Application of electrochemical methods for studying steel corrosion in alkali-activated materials
Application of electrochemical methods for studying steel corrosion in alkali‐activated materials
Application of electrical fields on textile-reinforced mortar interlayers for leakage detection and prevention of chloride-induced corrosion damages
Effect of chloride ion concentration on stress corrosion cracking and electrochemical corrosion of high manganese steel
Impact of cracks on distribution of chloride-induced reinforcement corrosion
Corrosion, stress corrosion cracking and corrosion fatigue behavior of magnesium alloy bioimplants
Corrosion reviews
Chloride‐induced steel corrosion in alkali‐activated fly ash mortar: Increased propensity for corrosion initiation at defects
Steel corrosion in reinforced alkali‐activated materials
Leaching, carbonation and chloride ingress in reinforced alkali-activated fly ash mortars
Predicting and understanding corrosion in molten chloride salts
Application of electrochemical methods for studying steel corrosion in alkali-activated materials
Application of electrochemical methods for studying steel corrosion in alkali-activated materials
Application of electrochemical methods for studying steel corrosion in alkali‐activated materials
Application of electrical fields on textile-reinforced mortar interlayers for leakage detection and prevention of chloride-induced corrosion damages
Effect of chloride ion concentration on stress corrosion cracking and electrochemical corrosion of high manganese steel
Impact of cracks on distribution of chloride-induced reinforcement corrosion
Corrosion, stress corrosion cracking and corrosion fatigue behavior of magnesium alloy bioimplants
Corrosion reviews
Chloride‐induced steel corrosion in alkali‐activated fly ash mortar: Increased propensity for corrosion initiation at defects
Steel corrosion in reinforced alkali‐activated materials
Leaching, carbonation and chloride ingress in reinforced alkali-activated fly ash mortars
Predicting and understanding corrosion in molten chloride salts
Application of electrochemical methods for studying steel corrosion in alkali-activated materials
Application of electrochemical methods for studying steel corrosion in alkali-activated materials
Application of electrochemical methods for studying steel corrosion in alkali‐activated materials
Application of electrical fields on textile-reinforced mortar interlayers for leakage detection and prevention of chloride-induced corrosion damages
Effect of chloride ion concentration on stress corrosion cracking and electrochemical corrosion of high manganese steel
Impact of cracks on distribution of chloride-induced reinforcement corrosion
Corrosion, stress corrosion cracking and corrosion fatigue behavior of magnesium alloy bioimplants