Realistic Evaluation of Reinforcement Bond Strength in Alkali-Activated Slag Concrete Exposed to Elevated Temperature
- Standort
-
Deutsche Nationalbibliothek Frankfurt am Main
- Umfang
-
Online-Ressource, 1 online resource.
- Sprache
-
Englisch
- Erschienen in
-
Realistic Evaluation of Reinforcement Bond Strength in Alkali-Activated Slag Concrete Exposed to Elevated Temperature ; volume:17 ; number:1 ; day:19 ; month:6 ; year:2023 ; pages:1-23 ; date:12.2023
International journal of concrete structures and materials ; 17, Heft 1 (19.6.2023), 1-23, 12.2023
- Urheber
-
Amer, Ismail
Kohail, Mohamed
El-Feky, M. S.
Rashad, Ahmed
Khalaf, Mohamed A.
- Beteiligte Personen und Organisationen
-
SpringerLink (Online service)
- DOI
-
10.1186/s40069-023-00596-2
- URN
-
urn:nbn:de:101:1-2023090412190270527545
- Rechteinformation
-
Open Access; Der Zugriff auf das Objekt ist unbeschränkt möglich.
- Letzte Aktualisierung
-
14.08.2025, 10:49 MESZ
Datenpartner
Dieses Objekt wird bereitgestellt von:
Deutsche Nationalbibliothek. Bei Fragen zum Objekt wenden Sie sich bitte an den Datenpartner.
Deutsche Nationalbibliothek. Bei Fragen zum Objekt wenden Sie sich bitte an den Datenpartner.
Beteiligte
- Amer, Ismail
- Kohail, Mohamed
- El-Feky, M. S.
- Rashad, Ahmed
- Khalaf, Mohamed A.
- SpringerLink (Online service)
Ähnliche Objekte (12)
Optimal design of ferronickel slag alkali-activated mortar for repair exposed to high thermal load
Durability of slag-based alkali-activated materials: A critical review
Carbonation Resistance of Alkali-Activated Slag Under Natural and Accelerated Conditions
Durability of alkali-activated fly ash-slag concrete- state of art
Revolutionizing Waste Management: Solidification of Landfill Leachates Using Alkali-Activated Slag
Performance of CO2-Cured Alkali-Activated Slag Pastes During Curing and Exposure
Factors affecting the drying shrinkage of alkali-activated slag/fly ash mortars
Durability of the Reinforced One-Part Alkali-Activated Slag Mortars with Different Fibers
Utilization of basalt fabrics as reinforcement for alkali-activated blast furnace slag systems
Evaluation of copper slag and stainless steel slag as replacements for blast furnace slag in binary and ternary alkali-activated cements
Comparison of One-Part and Two-Part Alkali-Activated Metakaolin and Blast Furnace Slag
Influence of slag composition on the stability of steel in alkali-activated cementitious materials
Optimal design of ferronickel slag alkali-activated mortar for repair exposed to high thermal load
Durability of slag-based alkali-activated materials: A critical review
Carbonation Resistance of Alkali-Activated Slag Under Natural and Accelerated Conditions
Durability of alkali-activated fly ash-slag concrete- state of art
Revolutionizing Waste Management: Solidification of Landfill Leachates Using Alkali-Activated Slag
Performance of CO2-Cured Alkali-Activated Slag Pastes During Curing and Exposure
Factors affecting the drying shrinkage of alkali-activated slag/fly ash mortars
Durability of the Reinforced One-Part Alkali-Activated Slag Mortars with Different Fibers
Utilization of basalt fabrics as reinforcement for alkali-activated blast furnace slag systems
Evaluation of copper slag and stainless steel slag as replacements for blast furnace slag in binary and ternary alkali-activated cements
Comparison of One-Part and Two-Part Alkali-Activated Metakaolin and Blast Furnace Slag
Influence of slag composition on the stability of steel in alkali-activated cementitious materials
Optimal design of ferronickel slag alkali-activated mortar for repair exposed to high thermal load
Durability of slag-based alkali-activated materials: A critical review
Carbonation Resistance of Alkali-Activated Slag Under Natural and Accelerated Conditions
Durability of alkali-activated fly ash-slag concrete- state of art
Revolutionizing Waste Management: Solidification of Landfill Leachates Using Alkali-Activated Slag
Performance of CO2-Cured Alkali-Activated Slag Pastes During Curing and Exposure
Factors affecting the drying shrinkage of alkali-activated slag/fly ash mortars
Durability of the Reinforced One-Part Alkali-Activated Slag Mortars with Different Fibers
Utilization of basalt fabrics as reinforcement for alkali-activated blast furnace slag systems
Evaluation of copper slag and stainless steel slag as replacements for blast furnace slag in binary and ternary alkali-activated cements
Comparison of One-Part and Two-Part Alkali-Activated Metakaolin and Blast Furnace Slag