Chalcopyrite Leaching in a Dimethyl Sulfoxide Solution Containing Copper Chloride
- Standort
-
Deutsche Nationalbibliothek Frankfurt am Main
- ISSN
-
2524-3470
- Umfang
-
Online-Ressource
- Sprache
-
Englisch
- Anmerkungen
-
online resource.
- Erschienen in
-
Chalcopyrite Leaching in a Dimethyl Sulfoxide Solution Containing Copper Chloride ; day:12 ; month:3 ; year:2021 ; pages:1-9
Mining, metallurgy & exploration ; (12.3.2021), 1-9
- Urheber
-
Takatori, Kota
Kato, Hidekazu
Yoshimura, Akihiro
Matsuno, Yasunari
- Beteiligte Personen und Organisationen
-
SpringerLink (Online service)
- DOI
-
10.1007/s42461-021-00400-3
- URN
-
urn:nbn:de:101:1-2021051322471123471686
- Rechteinformation
-
Open Access; Der Zugriff auf das Objekt ist unbeschränkt möglich.
- Letzte Aktualisierung
-
14.08.2025, 10:54 MESZ
Datenpartner
Dieses Objekt wird bereitgestellt von:
Deutsche Nationalbibliothek. Bei Fragen zum Objekt wenden Sie sich bitte an den Datenpartner.
Deutsche Nationalbibliothek. Bei Fragen zum Objekt wenden Sie sich bitte an den Datenpartner.
Beteiligte
- Takatori, Kota
- Kato, Hidekazu
- Yoshimura, Akihiro
- Matsuno, Yasunari
- SpringerLink (Online service)
Ähnliche Objekte (12)
Dioctadecyl dimethyl ammonium chloride (DODMAC) and Dihydrogenated tallow alkyl dimethyl ammonium chloride (DHTDMAC)
The Reductive Leaching of Chalcopyrite by Chromium (II) Chloride for the Rapid and Complete Extraction of Copper
Impact of leaching on chloride ingress profiles in concrete
Leaching Titaniferous Magnetite Concentrate by Alkaline Aqueous Solution
Leaching, carbonation and chloride ingress in reinforced alkali-activated fly ash mortars
Durability of clinker reduced shotcrete: Ca2+ leaching, sintering, carbonation and chloride penetration
Iron Chloride Vapor Treatment for Leaching Platinum Group Metals from Spent Catalysts
Process related copper leaching during a combined wood preservation process
Studies of the Anaerobic Leaching of Iron and Copper Containing Dump Material and Comparison to Chemical Leaching
Kinetics of copper leaching from direct-to-blister copper flash smelting slag by sulfuric acid
Surface Nanostructuring of Copper Using Fluoride and Chloride
Leaching of Trace Amounts of Metals from Flotation Tailings in Cupric Chloride Solutions
Dioctadecyl dimethyl ammonium chloride (DODMAC) and Dihydrogenated tallow alkyl dimethyl ammonium chloride (DHTDMAC)
The Reductive Leaching of Chalcopyrite by Chromium (II) Chloride for the Rapid and Complete Extraction of Copper
Impact of leaching on chloride ingress profiles in concrete
Leaching Titaniferous Magnetite Concentrate by Alkaline Aqueous Solution
Leaching, carbonation and chloride ingress in reinforced alkali-activated fly ash mortars
Durability of clinker reduced shotcrete: Ca2+ leaching, sintering, carbonation and chloride penetration
Iron Chloride Vapor Treatment for Leaching Platinum Group Metals from Spent Catalysts
Process related copper leaching during a combined wood preservation process
Studies of the Anaerobic Leaching of Iron and Copper Containing Dump Material and Comparison to Chemical Leaching
Kinetics of copper leaching from direct-to-blister copper flash smelting slag by sulfuric acid
Surface Nanostructuring of Copper Using Fluoride and Chloride
Leaching of Trace Amounts of Metals from Flotation Tailings in Cupric Chloride Solutions
Dioctadecyl dimethyl ammonium chloride (DODMAC) and Dihydrogenated tallow alkyl dimethyl ammonium chloride (DHTDMAC)
The Reductive Leaching of Chalcopyrite by Chromium (II) Chloride for the Rapid and Complete Extraction of Copper
Impact of leaching on chloride ingress profiles in concrete
Leaching Titaniferous Magnetite Concentrate by Alkaline Aqueous Solution
Leaching, carbonation and chloride ingress in reinforced alkali-activated fly ash mortars
Durability of clinker reduced shotcrete: Ca2+ leaching, sintering, carbonation and chloride penetration
Iron Chloride Vapor Treatment for Leaching Platinum Group Metals from Spent Catalysts
Process related copper leaching during a combined wood preservation process
Studies of the Anaerobic Leaching of Iron and Copper Containing Dump Material and Comparison to Chemical Leaching
Kinetics of copper leaching from direct-to-blister copper flash smelting slag by sulfuric acid
Surface Nanostructuring of Copper Using Fluoride and Chloride