Cracking during High-Temperature Deformation of a High-Strength Polycrystalline CoNi-Base Superalloy
- Location
-
Deutsche Nationalbibliothek Frankfurt am Main
- Extent
-
Online-Ressource
- Language
-
Englisch
- Bibliographic citation
-
In: Metals 12.9 (2022): 1520.
- Event
-
Veröffentlichung
- (where)
-
Erlangen
- (who)
-
Friedrich-Alexander-Universität Erlangen-Nürnberg (FAU)
- (when)
-
2022
- Creator
-
Hausmann, Daniel
Freund, Lisa Patricia
Solís, Cecilia
Giese, Sven
Göken, Mathias
Gilles, Ralph
Neumeier, Steffen
- DOI
-
10.3390/met12091520
- URN
-
urn:nbn:de:bvb:29-opus4-202652
- Rights
-
Der Zugriff auf das Objekt ist unbeschränkt möglich.
- Last update
-
15.08.2025, 7:36 AM CEST
Data provider
This object is provided by:
Deutsche Nationalbibliothek. If you have any questions about the object, please contact the data provider.
Deutsche Nationalbibliothek. If you have any questions about the object, please contact the data provider.
Associated
- Hausmann, Daniel
- Freund, Lisa Patricia
- Solís, Cecilia
- Giese, Sven
- Göken, Mathias
- Gilles, Ralph
- Neumeier, Steffen
- Friedrich-Alexander-Universität Erlangen-Nürnberg (FAU)
Time of origin
- 2022
Other Objects (12)
Inhibiting weld cracking in high-strength aluminium alloys
Hydrogen-assisted cracking of GMA welded 960 MPa grade high-strength steels
Stresses in repair welding of high-strength steels—part 1: restraint and cold cracking risk
Stresses in repair welding of high-strength steels—part 1: restraint and cold cracking risk
Effect of cold deformation on the stress corrosion cracking resistance of a high-strength stainless steel
Universality of High-Strength Tensors
Hydrogen-assisted cracking in GMA welding of high-strength structural steels using the modified spray arc process
Hydrogen-assisted cracking in GMA welding of high-strength structural steels using the modified spray arc process
High strain rate behaviour of high-strength steel welds
On the Dwell-Fatigue Crack Propagation Behavior of a High-Strength Ni-Base Superalloy Manufactured by Selective Laser Melting
Microstructural Stability and Evolution in a New Polycrystalline Ni-Base Superalloy
Oxidation Behavior of the Polycrystalline Ni-Base Superalloy VDM® Alloy 780
Inhibiting weld cracking in high-strength aluminium alloys
Hydrogen-assisted cracking of GMA welded 960 MPa grade high-strength steels
Stresses in repair welding of high-strength steels—part 1: restraint and cold cracking risk
Stresses in repair welding of high-strength steels—part 1: restraint and cold cracking risk
Effect of cold deformation on the stress corrosion cracking resistance of a high-strength stainless steel
Universality of High-Strength Tensors
Hydrogen-assisted cracking in GMA welding of high-strength structural steels using the modified spray arc process
Hydrogen-assisted cracking in GMA welding of high-strength structural steels using the modified spray arc process
High strain rate behaviour of high-strength steel welds
On the Dwell-Fatigue Crack Propagation Behavior of a High-Strength Ni-Base Superalloy Manufactured by Selective Laser Melting
Microstructural Stability and Evolution in a New Polycrystalline Ni-Base Superalloy
Oxidation Behavior of the Polycrystalline Ni-Base Superalloy VDM® Alloy 780
Inhibiting weld cracking in high-strength aluminium alloys
Hydrogen-assisted cracking of GMA welded 960 MPa grade high-strength steels
Stresses in repair welding of high-strength steels—part 1: restraint and cold cracking risk
Stresses in repair welding of high-strength steels—part 1: restraint and cold cracking risk
Effect of cold deformation on the stress corrosion cracking resistance of a high-strength stainless steel
Universality of High-Strength Tensors
Hydrogen-assisted cracking in GMA welding of high-strength structural steels using the modified spray arc process
Hydrogen-assisted cracking in GMA welding of high-strength structural steels using the modified spray arc process
High strain rate behaviour of high-strength steel welds
On the Dwell-Fatigue Crack Propagation Behavior of a High-Strength Ni-Base Superalloy Manufactured by Selective Laser Melting
Microstructural Stability and Evolution in a New Polycrystalline Ni-Base Superalloy