On the impact of Cr and Ag additions on the grain boundary microchemistry, hydrogen permeability and environmentally assisted cracking mechanism of an Al-Zn-Mg-Cu-Zr 7xxx alloy
- Location
-
Deutsche Nationalbibliothek Frankfurt am Main
- Extent
-
Online-Ressource
- Language
-
Englisch
- Bibliographic citation
-
In: 10.1016/j.corsci.2025.112759
- Event
-
Veröffentlichung
- (where)
-
Aachen
- (who)
-
Universitätsbibliothek der RWTH Aachen
- (when)
-
2025
- Creator
-
Beyß, Oliver
Belkacemi, Lisa T.
Hantzsche, Kerstin
Curd, Matthew E.
Zander, Daniela
Akuata, Chijioke Kenneth
- DOI
-
10.18154/RWTH-2025-01265
- URN
-
urn:nbn:de:101:1-2502180108158.249003819966
- Rights
-
Der Zugriff auf das Objekt ist unbeschränkt möglich.
- Last update
- 15.08.2025, 5:21 AM UTC
Data provider
This object is provided by:
Deutsche Nationalbibliothek. If you have any questions about the object, please contact the data provider.
Deutsche Nationalbibliothek. If you have any questions about the object, please contact the data provider.
Associated
- Beyß, Oliver
- Belkacemi, Lisa T.
- Hantzsche, Kerstin
- Curd, Matthew E.
- Zander, Daniela
- Akuata, Chijioke Kenneth
- Universitätsbibliothek der RWTH Aachen
Time of origin
- 2025
Other Objects (12)
On-chip environmentally assisted cracking in thin freestanding SiO2 films
6th International conference on environmentally-assisted cracking (Reston, Washington, DC, USA, July 16–21, 2023)
3D characterisation of hydrogen environmentally assisted cracking during static loading of AA7449-T7651
Study on permeability evolution and damage mechanism along the EGS fracture in heat mining stage under thermal stress/cracking
Electromagnetic effects on cracking of anisotropic polytropes
Essays on measuring and promoting environmentally friendly mobility
Combined control of fluid adsorption capacity and initial permeability on coal permeability
Safe long-term operation in the context of environmental effects on fracture, fatigue and environmentally-assisted cracking : final report of the SAFE-I project
Safe long-term operation in the context of environmental effects on fracture, fatigue and environmentally-assisted cracking : final report of the SAFE-II project
Effect of carbon anode production parameters on anode cracking
Effect of Cracking on Corrosion of Steel in Concrete
Studies on the ammonia permeability of aquaporins
On-chip environmentally assisted cracking in thin freestanding SiO2 films
6th International conference on environmentally-assisted cracking (Reston, Washington, DC, USA, July 16–21, 2023)
3D characterisation of hydrogen environmentally assisted cracking during static loading of AA7449-T7651
Study on permeability evolution and damage mechanism along the EGS fracture in heat mining stage under thermal stress/cracking
Electromagnetic effects on cracking of anisotropic polytropes
Essays on measuring and promoting environmentally friendly mobility
Combined control of fluid adsorption capacity and initial permeability on coal permeability
Safe long-term operation in the context of environmental effects on fracture, fatigue and environmentally-assisted cracking : final report of the SAFE-I project
Safe long-term operation in the context of environmental effects on fracture, fatigue and environmentally-assisted cracking : final report of the SAFE-II project
Effect of carbon anode production parameters on anode cracking
Effect of Cracking on Corrosion of Steel in Concrete
Studies on the ammonia permeability of aquaporins
On-chip environmentally assisted cracking in thin freestanding SiO2 films
6th International conference on environmentally-assisted cracking (Reston, Washington, DC, USA, July 16–21, 2023)
3D characterisation of hydrogen environmentally assisted cracking during static loading of AA7449-T7651
Study on permeability evolution and damage mechanism along the EGS fracture in heat mining stage under thermal stress/cracking
Electromagnetic effects on cracking of anisotropic polytropes
Essays on measuring and promoting environmentally friendly mobility
Combined control of fluid adsorption capacity and initial permeability on coal permeability
Safe long-term operation in the context of environmental effects on fracture, fatigue and environmentally-assisted cracking : final report of the SAFE-I project
Safe long-term operation in the context of environmental effects on fracture, fatigue and environmentally-assisted cracking : final report of the SAFE-II project
Effect of carbon anode production parameters on anode cracking
Effect of Cracking on Corrosion of Steel in Concrete