Environmental Stress Cracking of High-Density Polyethylene Applying Linear Elastic Fracture Mechanics
- Location
-
Deutsche Nationalbibliothek Frankfurt am Main
- Extent
-
Online-Ressource
- Language
-
Englisch
- Bibliographic citation
-
In: Polymers, 14, S. 1-21
- Event
-
Veröffentlichung
- (where)
-
Berlin
- (who)
-
Bundesanstalt für Materialforschung und -prüfung (BAM)
- (when)
-
2022
- Creator
-
Thuy, Maximilian
Pedragosa-Rincon, M.
Niebergall, Ute
Oehler, H.
Alig, I.
Böhning, Martin
- DOI
-
10.3390/polym14122415
- URN
-
urn:nbn:de:kobv:b43-550476
- Rights
-
Der Zugriff auf das Objekt ist unbeschränkt möglich.
- Last update
-
25.03.2025, 1:42 PM CET
Data provider
This object is provided by:
Deutsche Nationalbibliothek. If you have any questions about the object, please contact the data provider.
Deutsche Nationalbibliothek. If you have any questions about the object, please contact the data provider.
Associated
- Thuy, Maximilian
- Pedragosa-Rincon, M.
- Niebergall, Ute
- Oehler, H.
- Alig, I.
- Böhning, Martin
- Bundesanstalt für Materialforschung und -prüfung (BAM)
Time of origin
- 2022
Other Objects (12)
Environmental stress cracking in high-density polyethylene container materials exposed to crop protection agents
Biodegradable High‐Density Polyethylene‐like Material
High‐Density Polyethylene with In‐Chain Photolyzable and Hydrolyzable Groups Enabling Recycling and Degradation
Relation of craze to crack length during slow crack growth phenomena in high‐density polyethylene
Mesostructuring of SiCN Materials and Catalysts via Microphase Separation Technique utilizing High-Density Polyethylene Blocks
Fracture mechanics investigation of autohesive interfacial interactions of polyethylene stretch wrap films
Modelling elongational viscosity overshoot and brittle fracture of low-density polyethylene melts
Combined impact of UV radiation and nitric acid on high‐density polyethylene containers as a laboratory test
Verdichtetes Wohnen : = High-density housing
Cracking the supergravity correlators
Thermal induced cracking of granite
Cracking the project management interview
Environmental stress cracking in high-density polyethylene container materials exposed to crop protection agents
Biodegradable High‐Density Polyethylene‐like Material
High‐Density Polyethylene with In‐Chain Photolyzable and Hydrolyzable Groups Enabling Recycling and Degradation
Relation of craze to crack length during slow crack growth phenomena in high‐density polyethylene
Mesostructuring of SiCN Materials and Catalysts via Microphase Separation Technique utilizing High-Density Polyethylene Blocks
Fracture mechanics investigation of autohesive interfacial interactions of polyethylene stretch wrap films
Modelling elongational viscosity overshoot and brittle fracture of low-density polyethylene melts
Combined impact of UV radiation and nitric acid on high‐density polyethylene containers as a laboratory test
Verdichtetes Wohnen : = High-density housing
Cracking the supergravity correlators
Thermal induced cracking of granite
Cracking the project management interview
Environmental stress cracking in high-density polyethylene container materials exposed to crop protection agents
Biodegradable High‐Density Polyethylene‐like Material
High‐Density Polyethylene with In‐Chain Photolyzable and Hydrolyzable Groups Enabling Recycling and Degradation
Relation of craze to crack length during slow crack growth phenomena in high‐density polyethylene
Mesostructuring of SiCN Materials and Catalysts via Microphase Separation Technique utilizing High-Density Polyethylene Blocks
Fracture mechanics investigation of autohesive interfacial interactions of polyethylene stretch wrap films
Modelling elongational viscosity overshoot and brittle fracture of low-density polyethylene melts
Combined impact of UV radiation and nitric acid on high‐density polyethylene containers as a laboratory test
Verdichtetes Wohnen : = High-density housing
Cracking the supergravity correlators
Thermal induced cracking of granite