Synthesis and Application of Dendriticlinear Polymer PAMAM-Si for Leather Fatliquoring Process

Konferenzbeitrag

Content: Environmental pollution caused by leather making is the primary concern in the development of leather industry. The use of safe, effective and multi-functional green chemical products has the advantages of reducing leather operations, increasing chemicals utilization, decreasing the environmental burden, improving leather quality. In this study, dendritic-linear polymers of PAMAM-Si 1G and PAMAM-Si 2G were applied to fatliquoring process, which were prepared by branching polysiloxane on the dendritic polyamide-amine (PAMAM). Then the emulsion properties, fatliquoring properties and fatliquoring mechanism were studied by EDS, SEM, XRD, TG and washing experiments. The conclusion was drawn that PAMAM-Si are weak alkali products with high emulsion stability. The particle size of PAMAM-Si 1G was 35.8 nm, and that of PAMAM-Si 2G was 26.7 nm. They can improve the softness, shrinkage temperature and physical and mechanical properties of leather. The softness of leather with PAMAM-Si 1G and PAMAM-Si 2G increased by 115.6% and 104.7% respectively. The shrinkage temperature of leather with PAMAM-Si 2G increased by 2.9℃. The Breaking elongation of leather with PAMAM-Si 1G and PAMAM-Si 2G increased by 38.6% and 32.4% respectively. At the same time, PAMAM-Si not only increased the distance and disorder of fiber but combined with collagen fiber through hydrogen bond, a certain amount of physical adsorption and covalent bond. Take-Away: 1. The dendritic-linear polymers of PAMAM-Si 1G and PAMAM-Si 2G were prepared by branching polysiloxane on the dendritic polyamide-amine (PAMAM). 2. PAMAM-Si can improve the softness, shrinkage temperature and physical and mechanical properties of leather. 3. PAMAM-Si not only increased the distance and disorder of fiber but combined with collagen fiber through hydrogen bond, a certain amount of physical adsorption and covalent bond.

Verweise und Beziehungen

• Verwandtes Objekt und Literatur: urn:nbn:de:bsz:14-qucosa2-340872 ; qucosa:34087

Klassifikation und Themen

• Thema: Ingenieurwissenschaften

Beteiligte, Orts- und Zeitangaben

• Ereignis: Geistige Schöpfung
• (wer): Wang, Xuechuan ; Sun, Siwei ; Wang, Haijun ; Li, Ji
• Ereignis: Herstellung
• (wer): International Union of Leather Technologists and Chemists Societies
• Ereignis: Veröffentlichung
• (wer): Verein für Gerberei-Chemie und -Technik e. V. ; Forschungsinstitut für Leder und Kunststoffbahnen (FILK) gGmbH

Weitere Informationen

• URN: urn:nbn:de:bsz:14-qucosa2-342875
• Letzte Aktualisierung: 14.03.2025, 08:16 MEZ