Direct deposition of proton exchange membranes enabling high performance hydrogen fuel cells

Abstract: We apply drop-on-demand inkjet printing to fabricate proton exchange membranes for polymer electrolyte fuel cells. This completely substitutes the commonly used membrane foil. A Nafion® dispersion is deposited directly onto the catalyst layers of anode and cathode gas diffusion electrodes, and the two electrodes are pressed together with the membrane layers facing each other. Fuel cells constructed utilizing this method reveal a thin overall membrane thickness of 8–25 μm and a good adhesion of membrane and catalyst layers. This results in a membrane ionic resistance of only 12.7 mΩ cm2 without compromising hydrogen crossover, which was determined to be less than 2 mA cm−2. We achieve a cell power density exceeding 4 W cm−2 with pure oxygen as cathode fuel, which, to our knowledge, is the highest reported power density with a Nafion® membrane hydrogen fuel cell. The membrane shows a stable performance over the entire range of reactant gas humidification from 0 to 100% relative humidity. Power densities exceeding 1.0 W cm−2 are achieved under dry operation with air as cathode fuel. A 576 hour combined mechanical and chemical accelerated stress test reveals no significant degradation in terms of hydrogen crossover, indicating a promising lifetime of the membrane

Angaben zum Objekt

• Standort: Deutsche Nationalbibliothek Frankfurt am Main
• Umfang: Online-Ressource
• Sprache: Englisch
• Anmerkungen: Journal of materials chemistry / A. 3 (2015), 11239-11245, doi 10.1039/C5TA01341K, issn: 2050-7496 ; IN COPYRIGHT http://rightsstatements.org/page/InC/1.0 rs

Klassifikation und Themen

• Klassifikation: Biowissenschaften, Biologie

Beteiligte, Orts- und Zeitangaben

• Ereignis: Veröffentlichung
• (wo): Freiburg
• (wer): Albert-Ludwigs-Universität Freiburg
• (wann): 2015
• Urheber: Breitwieser, Matthias ; Zengerle, Roland ; Thiele, Simon ; Klingele, Matthias
• Beteiligte Personen und Organisationen: BIOSS Centre for Biological Signalling Studies ; Professur für Anwendungsentwicklung ; Freiburger Zentrum für interaktive Werkstoffe und bioinspirierte Technologien ; Technische Fakultät ; Albert-Ludwigs-Universität Freiburg

Weitere Informationen

• DOI: 10.1039/C5TA01341K
• URN: urn:nbn:de:bsz:25-freidok-122016
• Rechteinformation: Der Zugriff auf das Objekt ist unbeschränkt möglich.
• Letzte Aktualisierung: 25.03.2025, 13:48 MEZ