A comparative study of the utilization of synthetic foaming agent and aluminum powder as pore-forming agents in lightweight geopolymer synthesis
- Standort
-
Deutsche Nationalbibliothek Frankfurt am Main
- Umfang
-
Online-Ressource
- Sprache
-
Englisch
- Erschienen in
-
A comparative study of the utilization of synthetic foaming agent and aluminum powder as pore-forming agents in lightweight geopolymer synthesis ; volume:17 ; number:1 ; year:2019 ; pages:629-638 ; extent:10
Open chemistry ; 17, Heft 1 (2019), 629-638 (gesamt 10)
- Urheber
-
Anggarini, Ufafa
Pratapa, Suminar
Purnomo, Victor
Sukmana, Ndaru Candra
- DOI
-
10.1515/chem-2019-0073
- URN
-
urn:nbn:de:101:1-2410161625340.403467139051
- Rechteinformation
-
Open Access; Der Zugriff auf das Objekt ist unbeschränkt möglich.
- Letzte Aktualisierung
- 15.08.2025, 07:37 MESZ
Datenpartner
Dieses Objekt wird bereitgestellt von:
Deutsche Nationalbibliothek. Bei Fragen zum Objekt wenden Sie sich bitte an den Datenpartner.
Deutsche Nationalbibliothek. Bei Fragen zum Objekt wenden Sie sich bitte an den Datenpartner.
Beteiligte
- Anggarini, Ufafa
- Pratapa, Suminar
- Purnomo, Victor
- Sukmana, Ndaru Candra
Ähnliche Objekte (12)
Fabrication of Aluminum Foams with Small Pore Size by Melt Foaming Method
Durability of lightweight oil-well geopolymer system in sulfate environment
Wood-geopolymer compatibility : experimental study on bond performance and the feasibility of using wood particles to produce lightweight geopolymer composite
Comparison between in-mould and grid-as-mould aluminum foaming process by induction heating
Effect of Expanded Glass Lightweight Aggregate on the Performance of Geopolymer Mortar at Elevated Temperatures
Development of fiber compound foaming agent and experimental study on application performance of foamed lightweight soil
Use of light-weight foaming polylactic acid as a lung-equivalent material in 3D printed phantoms
Laser-welded Dissimilar Steel-aluminum Seams for Automotive Lightweight Construction
Fabrication of Porous Aluminum with Controllable Open-Pore Fraction
Development of an Aluminum-Based Hybrid Billet Material for the Process-Integrated Foaming of Hollow Co-Extrusions
Optimization of pore structure and wet tribological properties of paper-based friction materials using chemical foaming technology
Utilization of multiwalled boron nitride nanotubes for the reinforcement of lightweight aluminum ribbons
Fabrication of Aluminum Foams with Small Pore Size by Melt Foaming Method
Durability of lightweight oil-well geopolymer system in sulfate environment
Wood-geopolymer compatibility : experimental study on bond performance and the feasibility of using wood particles to produce lightweight geopolymer composite
Comparison between in-mould and grid-as-mould aluminum foaming process by induction heating
Effect of Expanded Glass Lightweight Aggregate on the Performance of Geopolymer Mortar at Elevated Temperatures
Development of fiber compound foaming agent and experimental study on application performance of foamed lightweight soil
Use of light-weight foaming polylactic acid as a lung-equivalent material in 3D printed phantoms
Laser-welded Dissimilar Steel-aluminum Seams for Automotive Lightweight Construction
Fabrication of Porous Aluminum with Controllable Open-Pore Fraction
Development of an Aluminum-Based Hybrid Billet Material for the Process-Integrated Foaming of Hollow Co-Extrusions
Optimization of pore structure and wet tribological properties of paper-based friction materials using chemical foaming technology
Utilization of multiwalled boron nitride nanotubes for the reinforcement of lightweight aluminum ribbons
Fabrication of Aluminum Foams with Small Pore Size by Melt Foaming Method
Durability of lightweight oil-well geopolymer system in sulfate environment
Wood-geopolymer compatibility : experimental study on bond performance and the feasibility of using wood particles to produce lightweight geopolymer composite
Comparison between in-mould and grid-as-mould aluminum foaming process by induction heating
Effect of Expanded Glass Lightweight Aggregate on the Performance of Geopolymer Mortar at Elevated Temperatures
Development of fiber compound foaming agent and experimental study on application performance of foamed lightweight soil
Use of light-weight foaming polylactic acid as a lung-equivalent material in 3D printed phantoms
Laser-welded Dissimilar Steel-aluminum Seams for Automotive Lightweight Construction
Fabrication of Porous Aluminum with Controllable Open-Pore Fraction
Development of an Aluminum-Based Hybrid Billet Material for the Process-Integrated Foaming of Hollow Co-Extrusions
Optimization of pore structure and wet tribological properties of paper-based friction materials using chemical foaming technology