Hydrogen Embrittlement Susceptibility of Gas Metal Arc Welded Joints from a High‐Strength Low‐Alloy Steel Grade S690QL
Herein, the hydrogen embrittlement (HE) susceptibility of base material and gas metal arc welds from a high‐strength low‐alloy steel grade S690QL by slow strain rate test (SSRT) with in situ hydrogen charging is investigated. To investigate the influence of welding process parameters on the HE susceptibility of welded joints, gas metal arc welds in multilayer technique with two different heat inputs are conducted. The results reveal a considerable loss of fracture elongation for all hydrogen‐charged specimens when compared with the uncharged reference conditions. If the higher heat input is chosen, the required minimum yield strength in the weld metal (WM) is not achieved. It is remarkable that this WM also revealed increased HE susceptibility as measured by the relative elongation loss, despite its higher ductility associated with the lower strength level. In combination with hydrogen measurements and fracture surface analysis, the crack propagation mechanisms and related HE mechanisms are intensively discussed.
- Standort
-
Deutsche Nationalbibliothek Frankfurt am Main
- Umfang
-
Online-Ressource
- Sprache
-
Englisch
- Erschienen in
-
Hydrogen Embrittlement Susceptibility of Gas Metal Arc Welded Joints from a High‐Strength Low‐Alloy Steel Grade S690QL ; volume:91 ; number:11 ; year:2020 ; extent:12
Steel research international ; 91, Heft 11 (2020) (gesamt 12)
- Urheber
- DOI
-
10.1002/srin.202000131
- URN
-
urn:nbn:de:101:1-2022063008081318373834
- Rechteinformation
-
Open Access; Der Zugriff auf das Objekt ist unbeschränkt möglich.
- Letzte Aktualisierung
- 15.08.2025, 07:31 MESZ
Datenpartner
Dieses Objekt wird bereitgestellt von:
Deutsche Nationalbibliothek. Bei Fragen zum Objekt wenden Sie sich bitte an den Datenpartner.
Deutsche Nationalbibliothek. Bei Fragen zum Objekt wenden Sie sich bitte an den Datenpartner.
Beteiligte
- Christ, Martin
- Guo, Xiaofei
- Sharma, Rahul
- Li, Tianyi
- Bleck, Wolfgang
- Reisgen, Uwe
Ähnliche Objekte (12)
Hydrogen Embrittlement Susceptibility of Gas Metal Arc Welded Joints from a High-Strength Low-Alloy Steel Grade S690QL
An investigation of microstructure and mechanical properties of low carbon steels subjected to welding
Untersuchungen über die Rekristallisation von Cu und AlMn 1 mit Hilfe von Volumen- und Anzahlverteilungen
Investigations on Hydrogen Embrittlement of Advanced High Strength Steels for Automotive Applications
Influence of mill scale on weld bead geometry and thermal cycle during GTA welding of high-strength steels
Charakterisierung und Optimierung des makoskopischen Reinheitsgrades in hochbeanspruchten Stählen durch Einsatz der US-Tauchtechnik-Prüfung : IGF-Nr. 14645 N = Characterisation and optimisation of macroscopic and mircoscopic internal cleanliness level in high-loaded steels through ultra sonic immersion system testing
Metallkundliche Auswirkungen von Energiesparmassnahmen im Bereich des Warmbandwerkes auf die Eigenschaften von kaltgewalzten Stählen : Forschungsvertrag Nr. 7210-EA/122 (1.9.1986 - 31.8.1990) ; Abschlussbericht
Bedeutung der Umformtemperatur und -geschwindigkeit bei der Blechumformung austenitischer Edelstähle : Ergebnisse eines Vorhabens der industriellen Gemeinschaftsförderung (IGF)
Multiscale modeling
Tempering and Intercritical Annealing of Air‐Hardening 4 wt% Medium Manganese Steels
New insights into the properties of high-manganese steel
New insights into the properties of high-manganese steel
Hydrogen Embrittlement Susceptibility of Gas Metal Arc Welded Joints from a High-Strength Low-Alloy Steel Grade S690QL
An investigation of microstructure and mechanical properties of low carbon steels subjected to welding
Untersuchungen über die Rekristallisation von Cu und AlMn 1 mit Hilfe von Volumen- und Anzahlverteilungen
Investigations on Hydrogen Embrittlement of Advanced High Strength Steels for Automotive Applications
Influence of mill scale on weld bead geometry and thermal cycle during GTA welding of high-strength steels
Charakterisierung und Optimierung des makoskopischen Reinheitsgrades in hochbeanspruchten Stählen durch Einsatz der US-Tauchtechnik-Prüfung : IGF-Nr. 14645 N = Characterisation and optimisation of macroscopic and mircoscopic internal cleanliness level in high-loaded steels through ultra sonic immersion system testing
Metallkundliche Auswirkungen von Energiesparmassnahmen im Bereich des Warmbandwerkes auf die Eigenschaften von kaltgewalzten Stählen : Forschungsvertrag Nr. 7210-EA/122 (1.9.1986 - 31.8.1990) ; Abschlussbericht
Bedeutung der Umformtemperatur und -geschwindigkeit bei der Blechumformung austenitischer Edelstähle : Ergebnisse eines Vorhabens der industriellen Gemeinschaftsförderung (IGF)
Multiscale modeling
Tempering and Intercritical Annealing of Air‐Hardening 4 wt% Medium Manganese Steels
New insights into the properties of high-manganese steel
New insights into the properties of high-manganese steel
Hydrogen Embrittlement Susceptibility of Gas Metal Arc Welded Joints from a High-Strength Low-Alloy Steel Grade S690QL
An investigation of microstructure and mechanical properties of low carbon steels subjected to welding
Untersuchungen über die Rekristallisation von Cu und AlMn 1 mit Hilfe von Volumen- und Anzahlverteilungen
Investigations on Hydrogen Embrittlement of Advanced High Strength Steels for Automotive Applications
Influence of mill scale on weld bead geometry and thermal cycle during GTA welding of high-strength steels
Charakterisierung und Optimierung des makoskopischen Reinheitsgrades in hochbeanspruchten Stählen durch Einsatz der US-Tauchtechnik-Prüfung : IGF-Nr. 14645 N = Characterisation and optimisation of macroscopic and mircoscopic internal cleanliness level in high-loaded steels through ultra sonic immersion system testing
Metallkundliche Auswirkungen von Energiesparmassnahmen im Bereich des Warmbandwerkes auf die Eigenschaften von kaltgewalzten Stählen : Forschungsvertrag Nr. 7210-EA/122 (1.9.1986 - 31.8.1990) ; Abschlussbericht
Bedeutung der Umformtemperatur und -geschwindigkeit bei der Blechumformung austenitischer Edelstähle : Ergebnisse eines Vorhabens der industriellen Gemeinschaftsförderung (IGF)
Multiscale modeling
Tempering and Intercritical Annealing of Air‐Hardening 4 wt% Medium Manganese Steels
New insights into the properties of high-manganese steel