Effects of cellulose nanofibers on flexural behavior of carbon-fiber-reinforced polymer composites with delamination

Abstract: Understanding the influence of delamination defects on the damage evolution behavior of carbon-fiber-reinforced polymers (CFRPs) is crucial to improve their engineering applications. This study examined the flexural damage behaviors of CFRP composites by using a combination of acoustic emission (AE) and X-ray micro-computed tomography (micro-CT). Four specimens with different delamination defects and 0.1 wt% cellulose nanofibers (CNFs) were subjected to three-point bending tests. AE was employed to monitor the loading process, and then, micro-CT was utilized to detect the internal damage. The results showed that for the specimens with preset delamination defects near the surface, CNF-reinforced specimen exhibited no obvious enhancement effect on bending strength, and its cumulative acoustic energy decreased by 28% compared with that of CFRP specimens. For the specimen with preset delamination damage in the middle position, CNFs had an obvious enhancement effect on mechanical behavior, and the cumulative acoustic energy decreased by 43%. No obvious kink band was observed in the CNF-reinforced specimens, and during crack propagation, causing cracking and delamination damage was difficult. The results of micro-CT are consistent with those of AE. The results combined the combination of AE and micro-CT reflect the superiority of the hybrid detection system.

Standort
Deutsche Nationalbibliothek Frankfurt am Main
Umfang
Online-Ressource
Sprache
Englisch

Erschienen in
Effects of cellulose nanofibers on flexural behavior of carbon-fiber-reinforced polymer composites with delamination ; volume:30 ; number:1 ; year:2023 ; extent:15
Science and engineering of composite materials ; 30, Heft 1 (2023) (gesamt 15)

Urheber
Liu, Ran
Shen, Gongtian
Zhang, Pengfei
Yang, Sa
Zhou, Wei
Ye, Chao
Li, Qing

DOI
10.1515/secm-2022-0180
URN
urn:nbn:de:101:1-2023021613054501263797
Rechteinformation
Open Access; Der Zugriff auf das Objekt ist unbeschränkt möglich.
Letzte Aktualisierung
14.08.2025, 10:50 MESZ

Datenpartner

Dieses Objekt wird bereitgestellt von:
Deutsche Nationalbibliothek. Bei Fragen zum Objekt wenden Sie sich bitte an den Datenpartner.

Beteiligte

  • Liu, Ran
  • Shen, Gongtian
  • Zhang, Pengfei
  • Yang, Sa
  • Zhou, Wei
  • Ye, Chao
  • Li, Qing

Ähnliche Objekte (12)