Wear behavior of zirconia substrates against different antagonist materials
Zusammenfassung: Objective: This study assessed the wear behavior of different zirconia substrates with distinct surface roughness against different antagonist materials.Method: Hemisphere-shaped specimens (diameter of 5mm) constructed from different materials (VM9, Vintage ZR, IPS e.max Press and human enamel) were used as antagonists against plates of two zirconia materials (P-NANOZR, Cercon HT) with different surface roughness (smooth (Ra=0.01), moderate (Ra=0.1) and rough (Ra=1). Each group (n=7) was exposed to thermomechanical fatigue in a mastication simulator to simulate 5 years of clinical service. All specimens were scanned using a laser scanner and volumetric loss was quantified. Scanning electron microscopy was used to evaluate wear pattern, whereas Raman spectroscopy was employed to determine the crystalline property of zirconia specimens.
- Standort
-
Deutsche Nationalbibliothek Frankfurt am Main
- Umfang
-
Online-Ressource
- Sprache
-
Englisch
- Anmerkungen
-
Albert-Ludwigs-Universität Freiburg, Dissertation, 2016
- Schlagwort
-
Zirkoniumdioxid
Zahnschmelz
Zahnprothetik
Zahntechnik
- Ereignis
-
Veröffentlichung
- (wo)
-
Freiburg
- (wer)
-
Universität
- (wann)
-
2016
- Urheber
- Beteiligte Personen und Organisationen
- DOI
-
10.6094/UNIFR/10818
- URN
-
urn:nbn:de:bsz:25-freidok-108181
- Rechteinformation
-
Der Zugriff auf das Objekt ist unbeschränkt möglich.
- Letzte Aktualisierung
-
14.08.2025, 10:44 MESZ
Datenpartner
Dieses Objekt wird bereitgestellt von:
Deutsche Nationalbibliothek. Bei Fragen zum Objekt wenden Sie sich bitte an den Datenpartner.
Deutsche Nationalbibliothek. Bei Fragen zum Objekt wenden Sie sich bitte an den Datenpartner.
Objekttyp
- Hochschulschrift
Beteiligte
- Aldegheishem, Alhanoof
- Att, Wael
- Universität
Entstanden
- 2016
Ähnliche Objekte (12)
In vitro wear behavior characterization of zirconia substrates against enamel and ceramic antagonists
Quantitative analysis on the wear of monolithic zirconia crowns on antagonist teeth
Wear behaviour of lithography ceramic manufactured dental zirconia
Antagonist Enamel Wears More Than Ceramic Inlays
Wear of feldspathic-ceramic-veneered zirconia posterior FPDs after 10 years
Influence of Antagonist Material on Fatigue and Fracture Resistance of Zirconia Crowns
Harsh Sliding Wear of a Zirconia Ball against a-C:H Coated CoCrMo Disc in Hyaluronic Gel
Microstructural characterization of yttria-stabilized zirconia thermal barrier coatings grown on sapphire substrates
The Correlation of Surface Roughness Parameters of Zirconia and Lithium Disilicate with Steatite Wear
Zirconia-toughened alumina ceramic wear particles do not elicit inflammatory responses in human macrophages
Effects of dynamic aging on the wear and fracture strength of monolithic zirconia restorations
In vivo wear performance of highly cross-linked polyethylene vs. yttria stabilized zirconia and alumina stabilized zirconia at a mean seven-year follow-up
In vitro wear behavior characterization of zirconia substrates against enamel and ceramic antagonists
Quantitative analysis on the wear of monolithic zirconia crowns on antagonist teeth
Wear behaviour of lithography ceramic manufactured dental zirconia
Antagonist Enamel Wears More Than Ceramic Inlays
Wear of feldspathic-ceramic-veneered zirconia posterior FPDs after 10 years
Influence of Antagonist Material on Fatigue and Fracture Resistance of Zirconia Crowns
Harsh Sliding Wear of a Zirconia Ball against a-C:H Coated CoCrMo Disc in Hyaluronic Gel
Microstructural characterization of yttria-stabilized zirconia thermal barrier coatings grown on sapphire substrates
The Correlation of Surface Roughness Parameters of Zirconia and Lithium Disilicate with Steatite Wear
Zirconia-toughened alumina ceramic wear particles do not elicit inflammatory responses in human macrophages
Effects of dynamic aging on the wear and fracture strength of monolithic zirconia restorations
In vivo wear performance of highly cross-linked polyethylene vs. yttria stabilized zirconia and alumina stabilized zirconia at a mean seven-year follow-up
In vitro wear behavior characterization of zirconia substrates against enamel and ceramic antagonists
Quantitative analysis on the wear of monolithic zirconia crowns on antagonist teeth
Wear behaviour of lithography ceramic manufactured dental zirconia
Antagonist Enamel Wears More Than Ceramic Inlays
Wear of feldspathic-ceramic-veneered zirconia posterior FPDs after 10 years
Influence of Antagonist Material on Fatigue and Fracture Resistance of Zirconia Crowns
Harsh Sliding Wear of a Zirconia Ball against a-C:H Coated CoCrMo Disc in Hyaluronic Gel
Microstructural characterization of yttria-stabilized zirconia thermal barrier coatings grown on sapphire substrates
The Correlation of Surface Roughness Parameters of Zirconia and Lithium Disilicate with Steatite Wear
Zirconia-toughened alumina ceramic wear particles do not elicit inflammatory responses in human macrophages
Effects of dynamic aging on the wear and fracture strength of monolithic zirconia restorations