Cavitation Studies on Type 304 Stainless Steel Subjected to Strain Controlled Fatigue Deformation
- Standort
-
Deutsche Nationalbibliothek Frankfurt am Main
- Umfang
-
Online-Ressource
- Sprache
-
Englisch
- Erschienen in
-
Cavitation Studies on Type 304 Stainless Steel Subjected to Strain Controlled Fatigue Deformation ; volume:8 ; number:4 ; year:1989 ; pages:217-224
High temperature materials and processes ; 8, Heft 4 (1989), 217-224
- Urheber
-
Rao,, K. Bhanu Sankara
Vijayalakshmi,, M.
Valsan,, M.
Mannan,, S.L.
Rodriguez,, P.
- DOI
-
10.1515/HTMP.1989.8.4.217
- URN
-
urn:nbn:de:101:1-2501260435336.951571194101
- Rechteinformation
-
Open Access; Der Zugriff auf das Objekt ist unbeschränkt möglich.
- Letzte Aktualisierung
-
15.08.2025, 07:30 MESZ
Datenpartner
Dieses Objekt wird bereitgestellt von:
Deutsche Nationalbibliothek. Bei Fragen zum Objekt wenden Sie sich bitte an den Datenpartner.
Deutsche Nationalbibliothek. Bei Fragen zum Objekt wenden Sie sich bitte an den Datenpartner.
Beteiligte
- Rao,, K. Bhanu Sankara
- Vijayalakshmi,, M.
- Valsan,, M.
- Mannan,, S.L.
- Rodriguez,, P.
Ähnliche Objekte (12)
Experimental study on cavitation in rubber vulcanizates subjected to constrained tensile deformation
Austenitic Stainless Steel EBF Subjected to Low and Extremely Low Cycle Fatigue
Basic Creep-Fatigue Models Considering Cavitation
Cavitation erosion resistance of 316L stainless steel fabricated using selective laser melting
Stainless and carbon steel bolts subjected to tension and shear loading
Cyclic deformation behavior of austenitic stainless steels in the very high cycle fatigue regime : Experimental results and mechanismbased simulations
Fatigue resistance of austenitic stainless steel bolts under tension
Hydrogen Embrittlement Mechanism in Fatigue of Austenitic Stainless Steels
Life-cycle cost analysis of bridges subjected to fatigue damage
Optimizing Stainless Steel Bearings: Enhancement of Stainless Steel Bearing Fatigue Life by Low-Temperature Forming
Microstructure Evolution During Hot Deformation of REX734 Austenitic Stainless Steel
Deformation and failure mechanism of excavation in clay subjected to hydraulic uplift
Experimental study on cavitation in rubber vulcanizates subjected to constrained tensile deformation
Austenitic Stainless Steel EBF Subjected to Low and Extremely Low Cycle Fatigue
Basic Creep-Fatigue Models Considering Cavitation
Cavitation erosion resistance of 316L stainless steel fabricated using selective laser melting
Stainless and carbon steel bolts subjected to tension and shear loading
Cyclic deformation behavior of austenitic stainless steels in the very high cycle fatigue regime : Experimental results and mechanismbased simulations
Fatigue resistance of austenitic stainless steel bolts under tension
Hydrogen Embrittlement Mechanism in Fatigue of Austenitic Stainless Steels
Life-cycle cost analysis of bridges subjected to fatigue damage
Optimizing Stainless Steel Bearings: Enhancement of Stainless Steel Bearing Fatigue Life by Low-Temperature Forming
Microstructure Evolution During Hot Deformation of REX734 Austenitic Stainless Steel
Deformation and failure mechanism of excavation in clay subjected to hydraulic uplift
Experimental study on cavitation in rubber vulcanizates subjected to constrained tensile deformation
Austenitic Stainless Steel EBF Subjected to Low and Extremely Low Cycle Fatigue
Basic Creep-Fatigue Models Considering Cavitation
Cavitation erosion resistance of 316L stainless steel fabricated using selective laser melting
Stainless and carbon steel bolts subjected to tension and shear loading
Cyclic deformation behavior of austenitic stainless steels in the very high cycle fatigue regime : Experimental results and mechanismbased simulations
Fatigue resistance of austenitic stainless steel bolts under tension
Hydrogen Embrittlement Mechanism in Fatigue of Austenitic Stainless Steels
Life-cycle cost analysis of bridges subjected to fatigue damage
Optimizing Stainless Steel Bearings: Enhancement of Stainless Steel Bearing Fatigue Life by Low-Temperature Forming
Microstructure Evolution During Hot Deformation of REX734 Austenitic Stainless Steel