- Location
-
Deutsche Nationalbibliothek Frankfurt am Main
- Extent
-
1 Online-Ressource.
- Language
-
Englisch
- Bibliographic citation
-
The dual role of dissolution at a crack tip ; volume:8 ; number:1 ; day:30 ; month:9 ; year:2024 ; pages:1-7 ; date:12.2024
npj Materials degradation ; 8, Heft 1 (30.9.2024), 1-7, 12.2024
- Creator
-
Zhao, Mingjie
Gu, Wenjia
Warner, Derek H.
- Contributor
-
SpringerLink (Online service)
- DOI
-
10.1038/s41529-024-00513-2
- URN
-
urn:nbn:de:101:1-2412152109564.761781771195
- Rights
-
Open Access; Der Zugriff auf das Objekt ist unbeschränkt möglich.
- Last update
-
15.08.2025, 7:27 AM CEST
Data provider
This object is provided by:
Deutsche Nationalbibliothek. If you have any questions about the object, please contact the data provider.
Deutsche Nationalbibliothek. If you have any questions about the object, please contact the data provider.
Associated
- Zhao, Mingjie
- Gu, Wenjia
- Warner, Derek H.
- SpringerLink (Online service)
Other Objects (12)
Modified Model of Crack Tip Stress Field Considering Dislocation Slip Accumulation and Crack Tip Blunting
An auxiliary crack approach for efficient approximative crack tip loading analyses
Generating porosity during olivine carbonation via dissolution channels and expansion cracks
Generating porosity during olivine carbonation via dissolution channels and expansion cracks
On the formation of expanding crack tip precipitates
Crack kinking at the tip of a mode I crack in an orthotropic solid
Crack tip shielding and size effect related to parallel edge cracks under uniaxial tensile loading
Modeling of crack-tip plasticity in tungsten single crystals
Modeling of crack-tip plasticity in tungsten single crystals
Explainable machine learning for precise fatigue crack tip detection
Explainable machine learning for precise fatigue crack tip detection
Dissolution
Modified Model of Crack Tip Stress Field Considering Dislocation Slip Accumulation and Crack Tip Blunting
An auxiliary crack approach for efficient approximative crack tip loading analyses
Generating porosity during olivine carbonation via dissolution channels and expansion cracks
Generating porosity during olivine carbonation via dissolution channels and expansion cracks
On the formation of expanding crack tip precipitates
Crack kinking at the tip of a mode I crack in an orthotropic solid
Crack tip shielding and size effect related to parallel edge cracks under uniaxial tensile loading
Modeling of crack-tip plasticity in tungsten single crystals
Modeling of crack-tip plasticity in tungsten single crystals
Explainable machine learning for precise fatigue crack tip detection
Explainable machine learning for precise fatigue crack tip detection
Dissolution
Modified Model of Crack Tip Stress Field Considering Dislocation Slip Accumulation and Crack Tip Blunting
An auxiliary crack approach for efficient approximative crack tip loading analyses
Generating porosity during olivine carbonation via dissolution channels and expansion cracks
Generating porosity during olivine carbonation via dissolution channels and expansion cracks
On the formation of expanding crack tip precipitates
Crack kinking at the tip of a mode I crack in an orthotropic solid
Crack tip shielding and size effect related to parallel edge cracks under uniaxial tensile loading
Modeling of crack-tip plasticity in tungsten single crystals
Modeling of crack-tip plasticity in tungsten single crystals
Explainable machine learning for precise fatigue crack tip detection
Explainable machine learning for precise fatigue crack tip detection