The influence of filler amount on selected properties of new experimental resin dental composite
Abstract: Aim of the study was to evaluate the influence of filler amounts on mechanical properties and contraction stress of light-curing experimental composite. Hardness, flexural strength, diametral tensile strength of material filled with 40, 50 or 60 wt. % of silanized silica were tested. The contraction stress was measured after 24 h by means of photoelastic study. The addition of 40-60 wt. % filler to composite caused significant increase in hardness, Young’s modulus and flexural strength. The DTS, after incorporating filler into polymer matrix, was valued at ~26 MPa. The composite containing 40 wt. % of filler demonstrated significantly lower contraction stress in comparison to neat resin and filled > 50 wt. % of silica.
- Standort
-
Deutsche Nationalbibliothek Frankfurt am Main
- Umfang
-
Online-Ressource
- Sprache
-
Englisch
- Erschienen in
-
The influence of filler amount on selected properties of new experimental resin dental composite ; volume:16 ; number:1 ; year:2018 ; pages:905-911 ; extent:7
Open chemistry ; 16, Heft 1 (2018), 905-911 (gesamt 7)
- Urheber
-
Bociong, Kinga
Szczesio, Agata
Krasowski, Michal
Sokolowski, Jerzy
- DOI
-
10.1515/chem-2018-0090
- URN
-
urn:nbn:de:101:1-2410161607504.155378088682
- Rechteinformation
-
Open Access; Der Zugriff auf das Objekt ist unbeschränkt möglich.
- Letzte Aktualisierung
-
15.08.2025, 07:39 MESZ
Datenpartner
Dieses Objekt wird bereitgestellt von:
Deutsche Nationalbibliothek. Bei Fragen zum Objekt wenden Sie sich bitte an den Datenpartner.
Deutsche Nationalbibliothek. Bei Fragen zum Objekt wenden Sie sich bitte an den Datenpartner.
Beteiligte
- Bociong, Kinga
- Szczesio, Agata
- Krasowski, Michal
- Sokolowski, Jerzy
Ähnliche Objekte (12)
Boron Nitride Nanotubes as Filler for Resin-Based Dental Sealants
Calcium hydroxyapatite nanoparticles as a reinforcement filler in dental resin nanocomposite
YbF3/SiO2 Fillers as Radiopacifiers in a Dental Adhesive Resin
Microtensile Bond Strength, Marginal Leakage, and Antibacterial Effect of Bulk Fill Resin Composite with Alkaline Fillers versus Incremental Nanohybrid Composite Resin
Dental biomaterials redefined: molecular docking and dynamics-driven dental resin composite optimization
Hydroxyapatite modified with polyhedral oligomeric silsesquioxane as a filler for dental resin-based composites
Trends in Resin Composite Restoration Repair Teaching in Dental Colleges in Pakistan
Treatment of Anterior Dental Crossbite Using Bonded Resin-Composite Slopes: Case Reports
Effect of roughness and acidic medium on wear behavior of dental resin composite
Beverage-Induced Surface Changes in Biomimetic Dental Resin Composite: AFM and Bacterial Analysis
The effect of surface sealants with different filler content on microleakage of Class V resin composite restorations
Antibacterial Silica Nanoparticles with PH-Sensitive Release Properties as Fillers for Dental Composite Materials
Boron Nitride Nanotubes as Filler for Resin-Based Dental Sealants
Calcium hydroxyapatite nanoparticles as a reinforcement filler in dental resin nanocomposite
YbF3/SiO2 Fillers as Radiopacifiers in a Dental Adhesive Resin
Microtensile Bond Strength, Marginal Leakage, and Antibacterial Effect of Bulk Fill Resin Composite with Alkaline Fillers versus Incremental Nanohybrid Composite Resin
Dental biomaterials redefined: molecular docking and dynamics-driven dental resin composite optimization
Hydroxyapatite modified with polyhedral oligomeric silsesquioxane as a filler for dental resin-based composites
Trends in Resin Composite Restoration Repair Teaching in Dental Colleges in Pakistan
Treatment of Anterior Dental Crossbite Using Bonded Resin-Composite Slopes: Case Reports
Effect of roughness and acidic medium on wear behavior of dental resin composite
Beverage-Induced Surface Changes in Biomimetic Dental Resin Composite: AFM and Bacterial Analysis
The effect of surface sealants with different filler content on microleakage of Class V resin composite restorations
Antibacterial Silica Nanoparticles with PH-Sensitive Release Properties as Fillers for Dental Composite Materials
Boron Nitride Nanotubes as Filler for Resin-Based Dental Sealants
Calcium hydroxyapatite nanoparticles as a reinforcement filler in dental resin nanocomposite
YbF3/SiO2 Fillers as Radiopacifiers in a Dental Adhesive Resin
Microtensile Bond Strength, Marginal Leakage, and Antibacterial Effect of Bulk Fill Resin Composite with Alkaline Fillers versus Incremental Nanohybrid Composite Resin
Dental biomaterials redefined: molecular docking and dynamics-driven dental resin composite optimization
Hydroxyapatite modified with polyhedral oligomeric silsesquioxane as a filler for dental resin-based composites
Trends in Resin Composite Restoration Repair Teaching in Dental Colleges in Pakistan
Treatment of Anterior Dental Crossbite Using Bonded Resin-Composite Slopes: Case Reports
Effect of roughness and acidic medium on wear behavior of dental resin composite
Beverage-Induced Surface Changes in Biomimetic Dental Resin Composite: AFM and Bacterial Analysis
The effect of surface sealants with different filler content on microleakage of Class V resin composite restorations