Effect of KCl on high‐temperature corrosion of low‐alloyed steel under low oxygen partial pressure
- Standort
-
Deutsche Nationalbibliothek Frankfurt am Main
- Umfang
-
Online-Ressource
- Sprache
-
Englisch
- Erschienen in
-
Effect of KCl on high‐temperature corrosion of low‐alloyed steel under low oxygen partial pressure ; day:15 ; month:05 ; year:2024 ; extent:8
Materials and corrosion ; (15.05.2024) (gesamt 8)
- Urheber
-
Moya Núñez, Alice
Norling, Rikard
- DOI
-
10.1002/maco.202414314
- URN
-
urn:nbn:de:101:1-2405151432259.717754159044
- Rechteinformation
-
Open Access; Der Zugriff auf das Objekt ist unbeschränkt möglich.
- Letzte Aktualisierung
-
14.08.2025, 10:51 MESZ
Datenpartner
Dieses Objekt wird bereitgestellt von:
Deutsche Nationalbibliothek. Bei Fragen zum Objekt wenden Sie sich bitte an den Datenpartner.
Deutsche Nationalbibliothek. Bei Fragen zum Objekt wenden Sie sich bitte an den Datenpartner.
Beteiligte
- Moya Núñez, Alice
- Norling, Rikard
Ähnliche Objekte (12)
A Comparative Study of the Initial Corrosion of KCl and PbCl2 on a Low-Alloyed Steel
The Influence of Oxide-Scale Microstructure on KCl(s)-Induced Corrosion of Low-Alloyed Steel at 400 °C
Hardening of Low-Alloyed Gold
Chlorine Corrosion Degradation of Low Alloyed Ferritic Steels in Temperature Range 450–550 °C
KCl-Induced High-Temperature Corrosion Behavior of HVAF-Sprayed Ni-Based Coatings in Ambient Air
Corrosion Studies of Low-Alloyed FeCrAl Steels in Liquid Lead at 750 °C
High‐temperature KCl‐induced corrosion of high Cr and Ni alloys investigated by in‐situ diffraction
High‐temperature KCl‐induced corrosion of high Cr and Ni alloys investigated by in‐situ diffraction
Effect of KCl deposits in high‐temperature corrosion on chromium‐rich steels in SO2‐containing atmosphere
Additive Manufacturing of a Low-alloyed Engineering Steel
Low irradiance multiphoton imaging with alloyed lanthanide nanocrystals
Effect of KCl deposits in high‐temperature corrosion on chromium‐rich steels in SO 2 ‐containing atmosphere
A Comparative Study of the Initial Corrosion of KCl and PbCl2 on a Low-Alloyed Steel
The Influence of Oxide-Scale Microstructure on KCl(s)-Induced Corrosion of Low-Alloyed Steel at 400 °C
Hardening of Low-Alloyed Gold
Chlorine Corrosion Degradation of Low Alloyed Ferritic Steels in Temperature Range 450–550 °C
KCl-Induced High-Temperature Corrosion Behavior of HVAF-Sprayed Ni-Based Coatings in Ambient Air
Corrosion Studies of Low-Alloyed FeCrAl Steels in Liquid Lead at 750 °C
High‐temperature KCl‐induced corrosion of high Cr and Ni alloys investigated by in‐situ diffraction
High‐temperature KCl‐induced corrosion of high Cr and Ni alloys investigated by in‐situ diffraction
Effect of KCl deposits in high‐temperature corrosion on chromium‐rich steels in SO2‐containing atmosphere
Additive Manufacturing of a Low-alloyed Engineering Steel
Low irradiance multiphoton imaging with alloyed lanthanide nanocrystals
Effect of KCl deposits in high‐temperature corrosion on chromium‐rich steels in SO 2 ‐containing atmosphere
A Comparative Study of the Initial Corrosion of KCl and PbCl2 on a Low-Alloyed Steel
The Influence of Oxide-Scale Microstructure on KCl(s)-Induced Corrosion of Low-Alloyed Steel at 400 °C
Hardening of Low-Alloyed Gold
Chlorine Corrosion Degradation of Low Alloyed Ferritic Steels in Temperature Range 450–550 °C
KCl-Induced High-Temperature Corrosion Behavior of HVAF-Sprayed Ni-Based Coatings in Ambient Air
Corrosion Studies of Low-Alloyed FeCrAl Steels in Liquid Lead at 750 °C
High‐temperature KCl‐induced corrosion of high Cr and Ni alloys investigated by in‐situ diffraction
High‐temperature KCl‐induced corrosion of high Cr and Ni alloys investigated by in‐situ diffraction
Effect of KCl deposits in high‐temperature corrosion on chromium‐rich steels in SO2‐containing atmosphere
Additive Manufacturing of a Low-alloyed Engineering Steel
Low irradiance multiphoton imaging with alloyed lanthanide nanocrystals