Phase-field study on microstructure formation in Mar-M247 during electron beam welding and correlation to hot cracking susceptibility
- Location
-
Deutsche Nationalbibliothek Frankfurt am Main
- Extent
-
Online-Ressource
- Language
-
Englisch
- Notes
-
In: 10.1088/1757-899X/861/1/012072
- Event
-
Veröffentlichung
- (where)
-
Aachen
- (who)
-
Universitätsbibliothek der RWTH Aachen
- (when)
-
2020
- Creator
-
Böttger, Bernd
Apel, Markus
Jokisch, T.
Senger, Aleksej
- DOI
-
10.18154/RWTH-2020-10022
- URN
-
urn:nbn:de:101:1-2021021702361185321670
- Rights
-
Der Zugriff auf das Objekt ist unbeschränkt möglich.
- Last update
-
15.08.2025, 7:29 AM CEST
Data provider
This object is provided by:
Deutsche Nationalbibliothek. If you have any questions about the object, please contact the data provider.
Deutsche Nationalbibliothek. If you have any questions about the object, please contact the data provider.
Associated
- Böttger, Bernd
- Apel, Markus
- Jokisch, T.
- Senger, Aleksej
- Universitätsbibliothek der RWTH Aachen
Time of origin
- 2020
Other Objects (12)
Investigation on hot cracking during laser welding by means of experimental and numerical methods
Hot cracking tendency of flux-cored arc welding with flux-cored wires of types Ni 6625
Hot cracking tendency of flux-cored arc welding with flux-cored wires of types Ni 6625
Process Optimization of Dual-Laser Beam Welding of Advanced Al-Li Alloys Through Hot Cracking Susceptibility Modeling
Prevention of solidification cracking during pulsed laser beam welding
On the relationship between the bulge effect and the hot cracking formation during deep penetration laser beam welding
Phase-Field Modelling of Welding and of Elasticity-Dependent Phase Transformations
Hot cracking phenomena in welds, 2. / Thomas Böllinghausen ... (ed.)
Hot cracking phenomena in welds, 3. / John Lippold ... (ed.)
A partitioned computational framework for damage evolution in stress corrosion cracking utilizing phase‐field
Modeling and computation of cracking in multiphase porous media with the phase-field approach
Numerical analysis of hot cracking in laser-hybrid welded tubes
Investigation on hot cracking during laser welding by means of experimental and numerical methods
Hot cracking tendency of flux-cored arc welding with flux-cored wires of types Ni 6625
Hot cracking tendency of flux-cored arc welding with flux-cored wires of types Ni 6625
Process Optimization of Dual-Laser Beam Welding of Advanced Al-Li Alloys Through Hot Cracking Susceptibility Modeling
Prevention of solidification cracking during pulsed laser beam welding
On the relationship between the bulge effect and the hot cracking formation during deep penetration laser beam welding
Phase-Field Modelling of Welding and of Elasticity-Dependent Phase Transformations
Hot cracking phenomena in welds, 2. / Thomas Böllinghausen ... (ed.)
Hot cracking phenomena in welds, 3. / John Lippold ... (ed.)
A partitioned computational framework for damage evolution in stress corrosion cracking utilizing phase‐field
Modeling and computation of cracking in multiphase porous media with the phase-field approach
Numerical analysis of hot cracking in laser-hybrid welded tubes
Investigation on hot cracking during laser welding by means of experimental and numerical methods
Hot cracking tendency of flux-cored arc welding with flux-cored wires of types Ni 6625
Hot cracking tendency of flux-cored arc welding with flux-cored wires of types Ni 6625
Process Optimization of Dual-Laser Beam Welding of Advanced Al-Li Alloys Through Hot Cracking Susceptibility Modeling
Prevention of solidification cracking during pulsed laser beam welding
On the relationship between the bulge effect and the hot cracking formation during deep penetration laser beam welding
Phase-Field Modelling of Welding and of Elasticity-Dependent Phase Transformations
Hot cracking phenomena in welds, 2. / Thomas Böllinghausen ... (ed.)
Hot cracking phenomena in welds, 3. / John Lippold ... (ed.)
A partitioned computational framework for damage evolution in stress corrosion cracking utilizing phase‐field
Modeling and computation of cracking in multiphase porous media with the phase-field approach