Effect of weld microstructure on brittle fracture initiation in the thermally-aged boiling water reactor pressure vessel head weld metal
- Location
-
Deutsche Nationalbibliothek Frankfurt am Main
- ISSN
-
1869-103X
- Extent
-
Online-Ressource
- Language
-
Englisch
- Notes
-
online resource.
- Bibliographic citation
-
Effect of weld microstructure on brittle fracture initiation in the thermally-aged boiling water reactor pressure vessel head weld metal ; volume:28 ; number:5 ; day:6 ; month:5 ; year:2021 ; pages:867-876 ; date:5.2021
International journal of minerals, metallurgy and materials ; 28, Heft 5 (6.5.2021), 867-876, 5.2021
- Creator
-
Hytönen, Noora
Que, Zai-qing
Arffman, Pentti
Lydman, Jari
Nevasmaa, Pekka
Ehrnstén, Ulla
Efsing, Pål
- Contributor
-
SpringerLink (Online service)
- DOI
-
10.1007/s12613-020-2226-6
- URN
-
urn:nbn:de:101:1-2021100119363960048608
- Rights
-
Open Access; Der Zugriff auf das Objekt ist unbeschränkt möglich.
- Last update
-
15.08.2025, 7:22 AM CEST
Data provider
This object is provided by:
Deutsche Nationalbibliothek. If you have any questions about the object, please contact the data provider.
Deutsche Nationalbibliothek. If you have any questions about the object, please contact the data provider.
Associated
- Hytönen, Noora
- Que, Zai-qing
- Arffman, Pentti
- Lydman, Jari
- Nevasmaa, Pekka
- Ehrnstén, Ulla
- Efsing, Pål
- SpringerLink (Online service)
Other Objects (12)
Weld 'Alī
Weld, C.
Weld, Margareta
Weld 'Alῑ
Laser weld spot detection based on YOLO-weld
Weld, Johann Caspar (Weber)
Indentation Plastometry of Welds
Effect of Hydrogen on the Stress Corrosion Cracking Behaviour in Alloy 182 Weld Metal Under Boiling Water Reactor Hydrogen Water Chemistry Conditions
Failure Characterization of Laser Welds and Spot Welds under Combined Loading Conditions
Modelling the weld cladding process to predict weld clad position and shape error
Grabmal für Kardinal Thomas Weld
White, Weld & Co., New York
Weld 'Alī
Weld, C.
Weld, Margareta
Weld 'Alῑ
Laser weld spot detection based on YOLO-weld
Weld, Johann Caspar (Weber)
Indentation Plastometry of Welds
Effect of Hydrogen on the Stress Corrosion Cracking Behaviour in Alloy 182 Weld Metal Under Boiling Water Reactor Hydrogen Water Chemistry Conditions
Failure Characterization of Laser Welds and Spot Welds under Combined Loading Conditions
Modelling the weld cladding process to predict weld clad position and shape error
Grabmal für Kardinal Thomas Weld
White, Weld & Co., New York
Weld 'Alī
Weld, C.
Weld, Margareta
Weld 'Alῑ
Laser weld spot detection based on YOLO-weld
Weld, Johann Caspar (Weber)
Indentation Plastometry of Welds
Effect of Hydrogen on the Stress Corrosion Cracking Behaviour in Alloy 182 Weld Metal Under Boiling Water Reactor Hydrogen Water Chemistry Conditions
Failure Characterization of Laser Welds and Spot Welds under Combined Loading Conditions
Modelling the weld cladding process to predict weld clad position and shape error
Grabmal für Kardinal Thomas Weld