The Comparison of Fracture Resistance between Low Translucent and Ultra-High Translucent Monolithic Zirconia Crown
Abstract: Objective From the beginning of its discovery, the monolithic zirconia crown was highlighted for its remarkable strength; therefore, only available in opaque color. During the past decade, the translucent monolithic zirconia crown was manufactured to meet the aesthetic and restoration demand but was thought to be the cause of decreasing its strength. This study aimed to compare the fracture resistance between two types of translucent monolithic zirconia crowns, that is, low translucent monolithic zirconia (LT) and ultra-high translucent monolithic zirconia (UHT). Material and Methods The premolar crown model was prepared using a computer-aided design/computer-aided manufacturing system, producing 1 mm of thickness. Ten crown samples were divided into LT and UHT. Then, each sample was measured for its fracture resistance using Universal Testing Machine until a fracture occurred. The differences in fracture resistance were analyzed using an independent t-test with p < 0.05. Result The LT showed a higher fracture resistance than UHT (p < 0.05). Conclusion The LT monolithic zirconia crown has strength and can be used for posterior crown restoration.
- Location
-
Deutsche Nationalbibliothek Frankfurt am Main
- Extent
-
Online-Ressource
- Language
-
Englisch
- Bibliographic citation
-
The Comparison of Fracture Resistance between Low Translucent and Ultra-High Translucent Monolithic Zirconia Crown ; volume:03 ; number:01/02 ; year:2022 ; pages:026-029
European dental research and biomaterials journal ; 03, Heft 01/02 (2022), 026-029
- Contributor
-
Tanudjaja, Pratama Kesuma
Bonifacius, Setyawan
Rikmasari, Rasmi
- DOI
-
10.1055/s-0043-1768175
- URN
-
urn:nbn:de:101:1-2024032111311826650203
- Rights
-
Open Access; Der Zugriff auf das Objekt ist unbeschränkt möglich.
- Last update
-
14.08.2025, 10:46 AM CEST
Data provider
Deutsche Nationalbibliothek. If you have any questions about the object, please contact the data provider.
Associated
- Tanudjaja, Pratama Kesuma
- Bonifacius, Setyawan
- Rikmasari, Rasmi
Other Objects (12)
In-vitro performance and fracture strength of thin monolithic zirconia crowns
Fracture Strength of Monolithic Zirconia Crowns with Modified Vertical Preparation: A Comparative In Vitro Study
Effect of Reduced Occlusal Thickness with Two Margin Designs on Fracture Resistance of Monolithic Zirconia Crowns
Fracture resistance of monolithic translucent zirconia crown bonded with different self-adhesive resin cement: influence of MDP-containing zirconia primer after aging
Quantitative analysis on the wear of monolithic zirconia crowns on antagonist teeth
Retention strength of monolithic zirconia crowns cemented with different primer-cement systems
Marginal gap and internal fit of 3D printed versus milled monolithic zirconia crowns
Trueness and precision of digital light processing fabricated 3D printed monolithic zirconia crowns
Fracture Resistance of Repaired 5Y-PSZ Zirconia Crowns after Endodontic Access
The Effect of Cyclic Loading On Fracture Strength of 3D Printed Zirconia Crowns and CAD/CAM Zirconia Crowns : An In-Vitro Study
Influence of Antagonist Material on Fatigue and Fracture Resistance of Zirconia Crowns
The influence of aging on the fracture load of milled monolithic crowns
In-vitro performance and fracture strength of thin monolithic zirconia crowns
Fracture Strength of Monolithic Zirconia Crowns with Modified Vertical Preparation: A Comparative In Vitro Study
Effect of Reduced Occlusal Thickness with Two Margin Designs on Fracture Resistance of Monolithic Zirconia Crowns
Fracture resistance of monolithic translucent zirconia crown bonded with different self-adhesive resin cement: influence of MDP-containing zirconia primer after aging
Quantitative analysis on the wear of monolithic zirconia crowns on antagonist teeth
Retention strength of monolithic zirconia crowns cemented with different primer-cement systems
Marginal gap and internal fit of 3D printed versus milled monolithic zirconia crowns
Trueness and precision of digital light processing fabricated 3D printed monolithic zirconia crowns
Fracture Resistance of Repaired 5Y-PSZ Zirconia Crowns after Endodontic Access
The Effect of Cyclic Loading On Fracture Strength of 3D Printed Zirconia Crowns and CAD/CAM Zirconia Crowns : An In-Vitro Study
Influence of Antagonist Material on Fatigue and Fracture Resistance of Zirconia Crowns
The influence of aging on the fracture load of milled monolithic crowns
In-vitro performance and fracture strength of thin monolithic zirconia crowns
Fracture Strength of Monolithic Zirconia Crowns with Modified Vertical Preparation: A Comparative In Vitro Study
Effect of Reduced Occlusal Thickness with Two Margin Designs on Fracture Resistance of Monolithic Zirconia Crowns
Fracture resistance of monolithic translucent zirconia crown bonded with different self-adhesive resin cement: influence of MDP-containing zirconia primer after aging
Quantitative analysis on the wear of monolithic zirconia crowns on antagonist teeth
Retention strength of monolithic zirconia crowns cemented with different primer-cement systems
Marginal gap and internal fit of 3D printed versus milled monolithic zirconia crowns
Trueness and precision of digital light processing fabricated 3D printed monolithic zirconia crowns
Fracture Resistance of Repaired 5Y-PSZ Zirconia Crowns after Endodontic Access
The Effect of Cyclic Loading On Fracture Strength of 3D Printed Zirconia Crowns and CAD/CAM Zirconia Crowns : An In-Vitro Study
Influence of Antagonist Material on Fatigue and Fracture Resistance of Zirconia Crowns