Stress Analysis and Creep Behavior of Service Exposed Primary Superheater Tube in a Thermal Power Plant
- Location
-
Deutsche Nationalbibliothek Frankfurt am Main
- Extent
-
Online-Ressource
- Language
-
Englisch
- Bibliographic citation
-
Stress Analysis and Creep Behavior of Service Exposed Primary Superheater Tube in a Thermal Power Plant ; volume:27 ; number:2 ; year:2008 ; pages:79-90
High temperature materials and processes ; 27, Heft 2 (2008), 79-90
- Creator
-
Ray,, Ashok Kumar
Diwakar,, Kumar
Sahu,, Jitendra Kumar
Das,, Hemant Kumar
Roy,, Nilima
Ghosh,, Rabindra Nath
- DOI
-
10.1515/HTMP.2008.27.2.79
- URN
-
urn:nbn:de:101:1-2501270426170.384641718505
- Rights
-
Open Access; Der Zugriff auf das Objekt ist unbeschränkt möglich.
- Last update
-
15.08.2025, 7:30 AM CEST
Data provider
This object is provided by:
Deutsche Nationalbibliothek. If you have any questions about the object, please contact the data provider.
Deutsche Nationalbibliothek. If you have any questions about the object, please contact the data provider.
Associated
- Ray,, Ashok Kumar
- Diwakar,, Kumar
- Sahu,, Jitendra Kumar
- Das,, Hemant Kumar
- Roy,, Nilima
- Ghosh,, Rabindra Nath
Other Objects (12)
Life Estimation and Creep Damage Quantification of Service Exposed Reformer Tube
Evaluation of creep behavior of extruded polystyrene load-bearing thermal insulation boards
Creep and Creep-rupture Behavior of 2124-T851 Aluminum Alloy
Influence of Media–Thermal Ageing on the Long‐Term Creep Behavior of Polypropylene
Thermal cycling creep of a fiber reinforced aluminum alloy
Thermal cycling creep of a fiber reinforced aluminum alloy
Creep and relaxation behavior of spring steel wires
Polymer selection for Eustachian tube stent application based on mechanical, thermal and degradation behavior
Creep and creep damage behavior of stainless steel 316L manufactured by laser powder bed fusion
Nanoindentation Characterization of Creep-fatigue Interaction on Local Creep Behavior of P92 Steel Welded Joint
Creep
Creep
Life Estimation and Creep Damage Quantification of Service Exposed Reformer Tube
Evaluation of creep behavior of extruded polystyrene load-bearing thermal insulation boards
Creep and Creep-rupture Behavior of 2124-T851 Aluminum Alloy
Influence of Media–Thermal Ageing on the Long‐Term Creep Behavior of Polypropylene
Thermal cycling creep of a fiber reinforced aluminum alloy
Thermal cycling creep of a fiber reinforced aluminum alloy
Creep and relaxation behavior of spring steel wires
Polymer selection for Eustachian tube stent application based on mechanical, thermal and degradation behavior
Creep and creep damage behavior of stainless steel 316L manufactured by laser powder bed fusion
Nanoindentation Characterization of Creep-fatigue Interaction on Local Creep Behavior of P92 Steel Welded Joint
Creep
Creep
Life Estimation and Creep Damage Quantification of Service Exposed Reformer Tube
Evaluation of creep behavior of extruded polystyrene load-bearing thermal insulation boards
Creep and Creep-rupture Behavior of 2124-T851 Aluminum Alloy
Influence of Media–Thermal Ageing on the Long‐Term Creep Behavior of Polypropylene
Thermal cycling creep of a fiber reinforced aluminum alloy
Thermal cycling creep of a fiber reinforced aluminum alloy
Creep and relaxation behavior of spring steel wires
Polymer selection for Eustachian tube stent application based on mechanical, thermal and degradation behavior
Creep and creep damage behavior of stainless steel 316L manufactured by laser powder bed fusion
Nanoindentation Characterization of Creep-fatigue Interaction on Local Creep Behavior of P92 Steel Welded Joint
Creep